PENGARUH UKURAN PARTIKEL OKSIDA PEROVSKIT TERHADAP MORFOLOGI DAN MUAI TERMAL MEMBRAN ASIMETRIS La0,6Sr0,4Co0,2Fe0,8O3-δ (LSCF 6428)

Pasicakti, Galuh Putri (2019) PENGARUH UKURAN PARTIKEL OKSIDA PEROVSKIT TERHADAP MORFOLOGI DAN MUAI TERMAL MEMBRAN ASIMETRIS La0,6Sr0,4Co0,2Fe0,8O3-δ (LSCF 6428). Other thesis, Institut Teknologi Sepuluh Nopember.

Text 27072019_Skripsi Galuh.pdf Restricted to Repository staff only Download (2MB) | Request a copy

Abstract

Tujuan dari penelitian ini adalah untuk mengkaji pengaruh ukuran partikel oksida perovskit yang dihasilkan dari dua metode sintesis yakni solid state dan kopresipitasi terhadap morfologi dan muai termal membran perovskit La0,6Sr0,4Co0,2Fe0,8O3-δ (LSCF 6428). Serbuk oksida perovskit dikarakterisasi menggunakan difraksi sinar-X (XRD), Particle Size Analysis (PSA), dan Scanning Electron Microscope (SEM). Karakterisasi dengan XRD menunjukkan bahwa kedua metode berhasil menghasilkan LSCF 6428. Metode solid state menghasilkan ukuran partikel sebesar 2812,4 nm yang lebih besar daripada kopresipitasi yakni sebesar 772,7 nm. Membran asimetris dipreparasi menggunakan metode inversi fasa dengan variasi ukuran partikel yakni ukuran besar (dari metode solid state), ukuran kecil (dari metode kopresipitasi) dan perpaduan ukuran partikel keduanya (1:1). Morfologi membran diamati dengan SEM dan koefisien muai termal membran diukur dengan Thermal Mechanical Analysis (TMA). Hasil SEM menunjukkan membran LSCF 6428 solid state memiliki struktur asimetris yang jelas dengan pola pori finger like dengan tingkat kerapatan yang lebih tinggi dibandingkan dengan dua membran yang lainnya. Pengukuran muai termal dengan TMA menunjukkan bahwa membran LSCF 6428 koprespitasi memiliki nilai koefisien muai termal yang stabil.
========================================================================
The purpose of this study was to examine the effect of perovskite oxide particle size produced by two synthesis methods, namely solid-state and coprecipitation, on the morphology and thermal expansion of the perovskite membrane La0.6Sr0.4Co0.2Fe0.8O3-δ (LSCF 6428). Perovskite oxide powder was characterized using X-ray diffraction (XRD), Particle Size Analysis (PSA), and Scanning Electron Microscope (SEM). XRD characterization showed that both methods successfully produced high-purity LSCF 6428. The solid-state method produced a particle size of 2812.4 nm, which was larger than that produced by the coprecipitation method, namely 772.7 nm. Asymmetric membranes were prepared using the phase inversion method with variations in particle size, namely large particles (from the solid-state method), small particles (from the coprecipitation method), and a combination of both particle sizes (1:1 ratio). Membrane morphology was characterized using SEM, while the thermal expansion coefficient was determined using Thermal Mechanical Analysis (TMA). SEM results indicated that the LSCF 6428 membrane prepared by the solid-state method exhibited a clear asymmetric structure with finger-like pores and a higher degree of densification than the other membranes. Thermal expansion measurements using TMA indicated that the LSCF 6428 membrane possessed a stable thermal expansion coefficient.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	La0,6Sr0,4Co0,2Fe0,8O3-δ, membran asimetris, solid state, kopresipitasi, ukuran partikel
Subjects:	Q Science > QD Chemistry > QD501 Catalysis. Catalysts.
Divisions:	Faculty of Natural Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	Galuh Putri Pasicakti
Date Deposited:	20 Jul 2026 06:00
Last Modified:	20 Jul 2026 06:00
URI:	http://repository.its.ac.id/id/eprint/66429

Actions (login required)

View Item