Setyawati, Maretta Zulfa (2019) Pengaruh Waktu Pengadukan Terhadap Ukuran Partikel Perovskit La0,6Sr0,4Co0,2Fe0,8O3-δ (LSCF 6428) yang Disintesis dengan Metode Kopresipitasi. Other thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
01211540000011-Undergraduate_Theses .pdf Download (1MB) | Preview |
Abstract
Perovskit La0,6Sr0,4Co0,2Fe0,8O3-δ (LSCF 6428) dengan variasi waktu pengadukan 0, 6, 12, 24 dan 30 jam berhasil disintesis dengan metode kopresipitasi. Hasil analisis TGA menunjukkan LSCF 6428 dapat terbentuk mulai suhu diatas 650 °C. Karakterisasi dengan difraksi sinar-X (XRD) menunjukkan LSCF 6428 memiliki struktur yang mirip dengan struktur LaCoO3. LSCF 6428 yang disintesis dengan variasi waktu pengadukan 0, 6, 12, dan 24 jam menghasilkan serbuk dengan kemurnian yang tinggi. Sementara terdapat fasa non perovskit pada waktu pengadukan 30 jam. Ukuran kristalit yang dihitung dengan persamaan Scherrer menunjukkan waktu pengadukan 6 jam memiliki ukuran kristalit terkecil (0,4317 nm) sementara waktu pengadukan 30 jam memiliki ukuran kristalit terbesar (0,5401 nm). Analisis Particle Size Analyzer (PSA) juga menunjukkan hasil serupa, yakni ukuran partikel terkecil dihasilkan dari pengadukan 6 jam (772,7 nm) dan terbesar pada waktu pengadukan 30 jam (1092,8 nm). Pengamatan dengan Scanning Electron Microscope (SEM) menunjukkan semua sampel memiliki bentuk partikel yang tidak beraturan dan dapat membentuk agregat. Variasi waktu pengadukan 24 jam dan 30 jam memiliki homogenitas ukuran yang lebih rendah daripada variasi lainnya.
===================================================================================================================================
Perovskite La0,6Sr0,4Co0,2F0,8O3-δ (LSCF 6428) with variations of stirring time 0, 6, 12, 24 and 30 hours were successfully synthesized by coprecipitation method. The results of the TGA analysis show LSCF 6428 can be formed from temperatures above 650 °C. Characterization with X-ray diffraction (XRD) shows LSCF 6428 has a structure similar to the LaCoO3 structure. LSCF 6428 which was synthesized with stirring time variations of 0, 6, 12, and 24 hours produced powder with high purity. While, there is a non perovskite phase at 30 hours stirring. The crystallite size calculated by the Scherrer equation shows the stirring time of 6 hours has the smallest crystal size (0,4317 nm) while the stirring time of 30 hours has the largest crystal size (0,5401 nm). Particle Size Analyzer (PSA) analysis also showed similar results, namely the smallest particle size generated from stirring 6 hours (772,7 nm) and the largest at 30 hours stirring (1092,8 nm). Observations with Scanning Electron Microscope (SEM) show that all samples have irregular particle shapes and can form aggregates. Variations in stirring time 24 hours and 30 hours have lower homogeneity in size than other variations.
| Item Type: | Thesis (Other) |
|---|---|
| Additional Information: | RSKi 549.5 Set p-1 2019 |
| Uncontrolled Keywords: | La0.6Sr0.4Co0.2F0.8O3-δ, Ukuran partikel, Kopresipitasi, Particle Size Analyzer (PSA) |
| Subjects: | Q Science > QD Chemistry Q Science > QD Chemistry > QD501 Catalysis. Catalysts. |
| Divisions: | Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47201-(S1) Undergraduate Thesis |
| Depositing User: | Maretta Zulfa Setyawati |
| Date Deposited: | 14 Jan 2025 06:54 |
| Last Modified: | 14 Jan 2025 06:54 |
| URI: | http://repository.its.ac.id/id/eprint/66658 |
Actions (login required)
 |
View Item |