Studi Eksperimen Pengaruh Variasi Kombinasi Elektroda Dan Sudut Groove Pengelasan Smaw Pada Baja ASTM A36 Terhadap Uji Metalografi, Uji Bending Dan Uji Impact

Hakim, Raditya Al (2019) Studi Eksperimen Pengaruh Variasi Kombinasi Elektroda Dan Sudut Groove Pengelasan Smaw Pada Baja ASTM A36 Terhadap Uji Metalografi, Uji Bending Dan Uji Impact. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 04311540000048_Undergraduate_Theses.pdf Restricted to Repository staff only Download (5MB) | Request a copy

Abstract

Baja ASTM A36 merupakan baja karbon rendah (Low Carbon) yang mempunyai karakteristik mudah untuk dijadikan bahan konstruksi bangunan laut maupun fabrikasi. Tujuan penelitian ini untuk mengetahui pengaruh variasi kombinasi elektroda dan sudut groove terhadap uji kekuatan tekuk, uji metalografi, uji impact pada pengelasan baja A36 dengan metode SMAW. Untuk elektroda yang digunakan adalah E-7016 dan E-7018. Kemudian untuk variasi sudut groove yang digunakan adalah 55 ̊, 65 ̊. Pada hasil uji tekuk menunjukkan bahwa semua spesimen tidak terdapat open defect maupun crack. Hasil pengamatan foto makro didapatkan hasil daerah HAZ yang terlebar adalah pada pengelasan dengan elekroda E 7018 dengan besar sudut groove 65 ̊, yaitu 22 mm. Sedangkan untuk hasil pengamatan mikro nya, pengelasan dengan elekroda E 7018 dengan besar sudut groove 65 ̊ mempunyai struktur ferritee terbesar yang terbentuk pada bagian weldmetal nya yaitu 77,8 %, sedangkan untuk struktur perlite yang terbentuk sebesar 22,2 %. Pada hasil pengujian impact menunjukkan bahwa nilai kekuatan impact yang tertinggi yaitu pada pengelasan dengan elektroda E 7018 dengan sudut groove 65 ̊ dibagian weldmetal sebesar 142 Joule. Sedangkan untuk nilai kekuatan yang terendah yaitu pada pengelasan dengan elektroda E 7016 dengan sudut groove 55 ̊ dibagian weldmetal sebesar 137 Joule.
============================================================
ASTM A36 steel is low carbon steel (Low Carbon) which has easy characteristics to be used as ship construction material and fabrication. The purpose of this study was to determine the effect of variations in the combination of electrodes and groove angles on bending strength test, metalographic test, impact resistance with the SMAW welding method. The electrodes used are E-7016 and E-7018. Then for variations in groove angles used are 55 ̊, 65 ̊. The results of the bending test indicate that all specimens have no open defects or cracks. The results of the macro photo observations obtained the widest HAZ region in welding with E 7018 electrode with a groove angle of 65 ̊, which is 22 mm. As for the micro-observation results, welding with E 7018 electrode with a groove angle of 65 ̊ has the largest ferrite structure formed in the weld metal part of 77.8%, while for the pearlite structure formed at 22.2%. The results of the impact test show that the highest impact strength value is in welding with E 7018 electrode with groove angle 65 ̊ weld at weldmetal section of 142 Joules. Whereas for the lowest strength value is welding with E 7016 electrode with groove angle 55 ̊ at weldmetal section at 137 Joules.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Baja A36, Elektroda, Sudut Groove, Shield Metal Arc Welding
Subjects:	T Technology > TN Mining engineering. Metallurgy > TN752.I5 Steel--Heat treatment T Technology > TS Manufactures > TS227 Welding.
Divisions:	Faculty of Marine Technology (MARTECH) > Ocean Engineering > 38201-(S1) Undergraduate Thesis
Depositing User:	Raditya Al Hakim
Date Deposited:	04 Jun 2026 04:52
Last Modified:	04 Jun 2026 04:52
URI:	http://repository.its.ac.id/id/eprint/67275

Actions (login required)

View Item