Analisis Kegagalan Low Temperature Superheater (LTSH) Tube pada Circulating Fluidized Bed (CFB) Boiler

Pratama, Wira Hamadri (2019) Analisis Kegagalan Low Temperature Superheater (LTSH) Tube pada Circulating Fluidized Bed (CFB) Boiler. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02111440000184-Undergraduated_Theses.pdf Restricted to Repository staff only Download (1MB) | Request a copy

Abstract

Boiler memiliki peranan penting di dalam pembangkit listrik tenaga uap di Indonesia. Pada pipa-pipa dan tube-tube boiler sering terjadi kegagalan terutama pada tube superheater. Tube superheater ini merupakan komponen dimana uap air dipanaskan sampai temperatur tinggi sehingga memiliki tekanan yang cukup untuk menggerakan generator pada pembangkit, hingga rentan akan terjadinya kegagalan. Superheater mengalami kerusakan berupa kebocoran (leaked) disebabkan penipisan dari tube. Dari hasil pengujian komposisi diketahui bahwa pipa superheater ini merupakan alloy Steel dengan tipe ASTM A213 grade T22. Tube yang di ambil pada penelitian mengalami kebocoran dan bulging dari sisi dalam tube. Pengamatan yang dilakuakn berupa pengamatan visual, mikrostruktur, dan kekerasam. Tube yang tidak mengalami kegagalan juga ikut diamati untuk dijadikan refrensi Hasil pengukuran ketebalan menunjukan adanya penipisan di dinding tube pada material ini. Pada pengujian hardness diketahui bahwa daerah masih baik memiliki kekerasan rata-rata 150 HV dan pada daerah yang mengalami kerusakan memiliki hasil uji kekerasan rata-rata sebesar 95 HV. Dari data SEM diketahui terdapat lapisan oksidasi yang ukuranya bervariasi pada setiap permukaan dalam tube. Lapisan oksida pada titik yang mengalami kegagalan mengandung unsur Ca, dimana unsur ini dapat mempercepat proses terjadinya lapisan oksida. Adanya lapisan oksida menyebabkan adanya kenaikan suhu tube sehingga menimbulkan creep pada rtuktur mikronya sebagai awal mula terjadinya kegagalan.
====================================================================================================================================
Boiler has an important role on steam power plant in Indonesia. In pipes and tubes of boiler especially on superheater part, failure is commonly found. The Superheater tube is a component where steam is heated until high temperature so it has enough pressure to move the generator on power plant Tube superheater ini merupakan komponen dimana uap air dipanaskan sampai temperatur tinggi sehingga memiliki tekanan yang cukup untuk menggerakan generator pada pembangkit, hingga rentan akan terjadinya kegagalan. The superheater tube has leakage due to thiniing from the tube. From chemical composition test it is known that the material of this superheater is steel with ASTM A213 grade T22. Tube that is taken on this research has leakage and bulging from inner side of the tube. Visual investigation, microstructure and hardness of the failure sample is investigated, along with sample that has no failure as reference. Thickess measurement indicates that on failure sample of the tube wall is thinning. In hardness testing it is known that on a non failure sample has average hardness of 150 HV, while for failure sample the results of average hardness value are 95 HV. from SEM data there is a known oxide layer that varies widely on each surface inside the tube. At the point of failure, the oxide layer has Ca elements, where this element could accelerate the formation of oxide layer. The presence of oxide layer caused the increase of temperature of the tube resulting in a creep in its microstructure as the beginning of failure.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	analisis kegagalan, superheater tube, leaked, oksidasi internal, creep
Subjects:	T Technology > TJ Mechanical engineering and machinery
Divisions:	Faculty of Industrial Technology > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User:	Pratama Wira Hamadri
Date Deposited:	21 Jul 2026 07:27
Last Modified:	21 Jul 2026 07:27
URI:	http://repository.its.ac.id/id/eprint/67683

Actions (login required)

View Item