Pengaruh Penambahan H-ZSM-5 Pada Fabrikasi Membran Komposit PMMA/H-ZSM-5 Sebagai Separator Baterai Ion Litium

Rahmat, Bima Maghfur Abdillah (2019) Pengaruh Penambahan H-ZSM-5 Pada Fabrikasi Membran Komposit PMMA/H-ZSM-5 Sebagai Separator Baterai Ion Litium. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 01211540000035-Undergraduate_Theses.pdf Restricted to Repository staff only Download (3MB) | Request a copy

Abstract

Membran komposit PMMA/H-ZSM-5 telah berhasil dibuat untuk digunakan sebagai separator baterai ion litium (LIBs). H-ZSM-5 yang digunakan merupakan hasil modifikasi ZSM-5 komersial melalui proses desilikasi untuk menghasilkan pori meso. Membran dikarakterisasi menggunakan XRD, FTIR, dan SEM untuk mengetahui karakter struktur kristalinitas, struktur ikatan dan morfologi membran. Konduktivitas ion diukur dengan EIS. Penggunaan H-ZSM-5 sebagai campuran komposit membran mengakibatkan pembentukan pori-pori permukaan membran yang lebih besar. Dari penelitian didapati membran dengan komposisi H-ZSM-5 lebih tinggi memiliki hubungan berbanding lurus dengan kemampuan kebasahan membran. Membran dengan resapan elektrolit yang lebih tinggi berkolerasi positif dengan kenaikan konduktivitas ion membran komposit. Hasilnya membran dengan kode ZP-20 memiliki konduktivitas ion tertinggi sebesar 1,32 x 10-4 S.cm-1.
===================================================================================================================================
PMMA/H-ZSM-5 composite membrane has been successfully fabricated to be used as lithium ion batteries (LIBs) separator. H-ZSM-5 gained from structure modification of ZSM-5 by desilication process to form mesoporous ZSM-5. The membrane is characterized by XRD, FTIR and SEM to know its cristalinity struture, bonding structure and morphology. Ionic conductivity is measured by EIS. ZSM-5 utilized as mixture of membrane composite makes larger surface pores formation. From the research, reported that higher H-ZSM-5 composition in composite membrane is directly proportional correlate to wettability of membrane. Higher electrolyte uptake of membrane correlate positively to membrane ionic conductivity increasement. As result, ZP-20 code membrane has highest ionic conductivity up to 1,32 x 10-4 S.cm-1.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Membran komposit PMMA/H-ZSM-5, Separator, Baterai ion litium (LIBs), Konduktivitas ion
Subjects:	Q Science Q Science > QD Chemistry Q Science > QD Chemistry > QD115 Electrochemical analysis Q Science > QD Chemistry > Polymerization
Divisions:	Faculty of Natural Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	Bima Maghfur Abdillah Rahmat
Date Deposited:	20 Jul 2026 04:19
Last Modified:	20 Jul 2026 04:19
URI:	http://repository.its.ac.id/id/eprint/69058

Actions (login required)

View Item