Studi Pengaruh Jenis Dan Komposisi Minyak Nabati Terhadap Morfologi Dan Sifat Mekanik Bioresin Vinil Ester Untuk Aplikasi Material Core Sandwich Pada Lambung Kapal

Sari, Eli Novita (2019) Studi Pengaruh Jenis Dan Komposisi Minyak Nabati Terhadap Morfologi Dan Sifat Mekanik Bioresin Vinil Ester Untuk Aplikasi Material Core Sandwich Pada Lambung Kapal. Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 02511750012005-Master_Thesis.pdf Restricted to Repository staff only Download (9MB) | Request a copy

Abstract

Minyak nabati merupakan alternatif untuk mengganti minyak mineral dan bahan kimia, karena minyak nabati bersifat biodegradable, tidak beracun, ramah lingkungan, dan dapat diperbarui. Bioresin didapatkan dari pencampuran polimer minyak nabati dengan polimer sintetis, salah satu jenis polimer sintetis adalah polimer vinil ester. Vinil ester adalah polimer termoseting yang menggabungkan sifat kimia, mekanik, dan termal melalui pembekuan cepat. Penelitian ini akan mengembangkan bioresin yang merupakan campuran dari polimer vinil ester dengan polimer alam berupa minyak nabati. Pengaplikasian bioresin tersebut akan digunakan sebagai bahan utama core sandwich. Core sandwich merupakan komponen yang terdiri dari 2 faceplate dan material inti yang akan diterapkan pada lambung kapal. Lambung kapal sebelumnya terbuat dari besi yang menyebabkan peningkatan beban internal kapal dan menurukan performa kapal. Pengujian yang dilakukan dalam penelitian ini meliputi uji kekerasan, pengujian tarik dan pertambahan panjang, pengujian tekuk, FTIR, SEM, TGA, massa jenis, dan daya serap air. Hasil dari pengujian dikonfirmasi sesuai standar BKI dan Lloyd Register. Hasil dari pengujian bioresin dengan variasi minyak nabati yang meliputi minyak sawit, minyak kelapa, minyak kedelai, dan minyak wijen didapatkan hasil bahwa bioresin vinil ester dengan pengisi minyak sawit (VE-MS) dan minyak wijen (VE-MW) memiliki properti teroptimum. Nilai kekerasan VE-MS 76 HD dan VE-MW 75 HD, nilai kekuatan tarik VE-MS 42 Mpa dan VE-MW 45 Mpa, nilai pertambahan panjang VE-MS 24% dan VE-MW 20%, nilai kekuatan tekuk VE-MS 73 Mpa dan VE-MW 89 Mpa, massa jenis VE-MS 1,004 g/cm3 dan VE-MW 1,003 g/cm3. Hasil dari pengujian bioresin dengan variasi komposisi minyak wijen dan minyak sawit didapatkan hasil nilai kekerasan semakin rendah dengan semakin banyaknya penambahan komposisi minyak nabati. Nilai kekuatan tarik menurun dengan bertambahnya komposisi minyak nabati, begitu pula dengan nilai pertambahan panjang yang meningkat dengan peningkatan komposisi minyak nabati. Kemudian, nilai kekuatan bending menurun dengan bertambahnya komposisi minyak nabati. Selanjutnya, untuk nilai massa jenis menunjukkan semakin banyak komposisi minyak nabati, nilai massa jenis semakin menurun.
=====================================================================================================================================
Vegetable oil (VO) is an alternative to replacing mineral oil and chemicals because vegetable oils are biodegradable, non-toxic, environmentally friendly and can be renewed. Bioresin is obtained from mixing vegetable oil polymers with synthetic polymers, one type of synthetic polymer is vinyl ester polymer. Vinyl esters are thermosetting polymers that combine chemical, mechanical and thermal properties through rapid freezing. This research will develop bio-resin which is a mixture of vinyl ester polymer with a natural polymer in the form of vegetable oil. The application of the bio-resin will be used as the main ingredient of core sandwiches. The core sandwich is a component consisting of 2 faceplates and the core material that will be applied to the hull of the ship. Previous hulls were made of iron which caused an increase in the ship's internal load and reduced ship performance. Tests carried out in this study include the hardness test, tensile and elongation test, bending test, FTIR, SEM, TGA, density, and water absorption. The results of the tests are confirmed according to the BKI and Lloyd Register standards. The results of bio-resin testing with a variety of vegetable oils including palm oil, coconut oil, soybean oil, and sesame oil showed that vinyl ester bio-resin with palm oil fillers (VE-PO) and sesame oil (VE-SO) had the best properties. VE-PO 76 HD and VE-SO 75 HD hardness values, VE-PO 42 Mpa tensile strength values and VE-SO 45 Mpa, VE-PO elongation values 24% and VE-SO 20%, VE-SO bending strength values 73 Mpa and VE-SO 89 Mpa, VE-PO density 1.004 g / cm3 and VE-SO 1.003 g /cm3. The results of bio-resin testing with variations in the composition of sesame oil and palm oil showed that the hardness value was getting lower with the increasing number of vegetable oil compositions. The value of tensile strength decreases with an increasing component of vegetable oils, as well as the value of elongation which is increased with an increase in the composition of vegetable oils. Then, the value of bending strength is decreased with an increasing component of vegetable oils. Furthermore, for the density type shows the more composition of vegetable oils, the value of density increases.

Item Type:	Thesis (Masters)
Uncontrolled Keywords:	Minyak Nabati, Vinil Ester, Bioresin, Core Sandwich, Mechanical Properties
Subjects:	T Technology > TP Chemical technology > TP1140 Polymers
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering > 27101-(S2) Master Thesis
Depositing User:	Sari Eli Novita
Date Deposited:	02 Jun 2026 02:25
Last Modified:	02 Jun 2026 02:25
URI:	http://repository.its.ac.id/id/eprint/69066