Pengaruh Komposisi SiO2 Dan Isopropanol Dalam Active Flux TiO2-SiO2 Menggunakan Solvent Methanol-Isopropanol Terhadap Karakteristik Penetrasi Pengelasan A-TIG Aluminum 5083-H116

Nugroho, Wisnu Yulianto (2019) Pengaruh Komposisi SiO2 Dan Isopropanol Dalam Active Flux TiO2-SiO2 Menggunakan Solvent Methanol-Isopropanol Terhadap Karakteristik Penetrasi Pengelasan A-TIG Aluminum 5083-H116. Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 02511750010007-Master_Thesis.pdf Restricted to Repository staff only Download (7MB) | Request a copy

Abstract

Proses pengelasan pada aluminium pada umumya dilakukan dengan proses las GTAW/TIG, karena memiliki hasil lasan yang bersih dan weld bead yang baik, akan tetapi penetrasi yang dihasilkan dari jenis pengelasan ini sangat rendah kurang dari 1 mm. Tujuan dari penelitian ini adalah untuk menyelidiki efek dari variasi komposisi active flux TiO2-SiO2 terhadap solvent Methanol-Isopropanol pada proses pengelasan A-TIG (Activated Tungsten Inert Gas) terhadap karateristik pengelasan yang meliputi DWR (Deep to Width Ratio), kekerasan dan perubahan struktur mikro. Logam induk yang digunakan adalah Aluminum seri 5083-H116 dengan variabel komposisi SiO2 terhadap paduan active flux TiO2-SiO2 (0%, 20%, 40%, 60%, 80%, dan 100%), hasil penelitian pada variabel pertama didapatkan sampel dengan komposisi 80% TiO2-20% SiO2 memiliki nilai DWR tertinggi dari hasil visual weld bead yang terbaik senilai 0.26 dengan kedalaman penetrasi 1.76 mm yang diikuti dengan bentuk butir halus, sedangkan untuk distribusi kekerasan rata-rata pada keseluruhan daerah pengelasan pada spesimen sebesar 91.61 HV, sedangkan pada variabel komposisi solvent nilai DWR yang paling baik ada pada spesimen dengan komposisi slovent 60% methanol- 40% Isopropanol, besaran nilai DWR yang didapat yaitu sebesar 0.43, dan distribusi kekerasan rata-rata pada keseluruhan daerah pengelasan pada spesimen sebesar 91.61 HV. Maka dari data yang diperoleh dalam penelitian ini dapat disimpulkan bahwa penambahan active flux TiO2-SiO2 memiliki efek yang signifikan dalam merubah geometri penetrasi lasan dan nilai kekerasannya, akan tetapi penambahan Isopropanol kedalam solvent memberikan efek penambahan penetrasi pada komposisi Isopropanol maksimal 40% pada solvent Methanol-Isopropanol. Oleh karena itu komposisi active flux 80% TiO2-20% SiO2 dengan solvent 60% methanol- 40% Isopropanol memberikan hasil yang terbaik pada penelitian ini ditinjau dari weld bead, nilai DWR, serta karakteristik pengelasannya.
==============================================================================================================================
The welding process on aluminum is generally carried out by the GTAW / TIG welding process, because it has good weld results and good bead welds, but the tests produced from this type of welding are very low less than 1 mm. The purpose of this study was to investigate the effects of variations in the composition of active flux TiO2-SiO2 against solvent Methanol-Isopropanol in the A-TIG (Activated Tungsten Inert Gas) welding process against welding characteristics which include DWR (Deep to Width Ratio), hardness and transformation of microstructure. The base metal used is Aluminum series 5083-H116 with variable composition of SiO2 on TiO2-SiO2 active flux alloys (0%, 20%, 40%, 60%, 80%, and 100%), the results of the first variable were obtained with the composition of 80% TiO2-20% SiO2 has the highest DWR value from the best visual weld bead value of 0.26 with a penetration depth of 1.76 mm followed by fine grain shape. while for the hardness distribution on average in the entire welding area of the specimen is 91.61 HV, while the variable solvent composition the best DWR value is in specimens with slovent 60% methanol-40% Isopropanol composition, the DWR value obtained is equal to 0.43, and the average distribution of hardness in the entire welding area of the specimen is 91.61 HV. Therefore from the data obtained in this study it can be concluded that the addition of TiO2-SiO2 active flux has a significant effect in changing the geometry of weld penetration and hardness value, but the addition of Isopropanol into the solvent has the effect of adding penetration to the composition of 40% maximum Isopropanol on solvent Methanol-Isopropanol. Therefore the composition of 80% active flux TiO2-20% SiO2 with solvent 60% methanol - 40% Isopropanol gives the best results in this study from the weld bead, DWR value, and welding characteristics.

Item Type:	Thesis (Masters)
Uncontrolled Keywords:	A-TIG, active flux, methanol, isopropanol, penetrasi.
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) T Technology > TS Manufactures
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering > 27101-(S2) Master Thesis
Depositing User:	NUGROHO WISNU YULIANTO
Date Deposited:	22 Jul 2026 04:37
Last Modified:	22 Jul 2026 04:37
URI:	http://repository.its.ac.id/id/eprint/69208

Actions (login required)

View Item