Pengembangan Ekstrak Daun Pepaya (Carica Papaya) Sebagai Inhibitor Korosi Pada Baja API 5L Grade B Dengan Variasi Temperatur Media Larutan HCL 1M

Putri, Rachmawati Hapsari (2019) Pengembangan Ekstrak Daun Pepaya (Carica Papaya) Sebagai Inhibitor Korosi Pada Baja API 5L Grade B Dengan Variasi Temperatur Media Larutan HCL 1M. Diploma thesis, Institut Teknologi Sepuluh Nopember.

Text 10211600000055-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (7MB) | Request a copy

Abstract

Korosi adalah perubahan sifat material khususnya logam akibat reaksi dengan lingkungan sekitarnya. Korosi cenderung bersifat menurunkan kualitas sifat mekanik material. Salah satu cara untuk menghambat korosi adalah dengan penambahan inhibitor. Inhibitor organik merupakan inhibitor yang dianggap ramah lingkungan. Dalam penelitian ini digunakan ekstrak daun pepaya sebagai inhibitor organik. Material yang digunakan adalah baja API 5L Grade B dalam larutan HCl 1M sebagai media korosif dengan variasi temperatur 30℃, 40℃ dan 50℃ sedangkan konsentrasi ekstrak yang digunakan pada penelitian ini sebesar 0mg-1000mg. Jenis pengujian yang dilakukan pada penelitian ini adalah EIS (Electrochemical Impedance Spectroscopy), PDP (Potentiodynamic Polarization), pengurangan berat (weight loss) dan Scanning Electron Microscopy (SEM). Hasil pengujian menunjukkan adanya penurunan laju korosi pada baja API 5L Grade B dalam larutan HCl 1M ketika ditambahkan inhibitor ekstrak daun pepaya. Pada pengujian polarisasi potensiodinamik didapatkan laju korosi pada sample tanpa inhibitor sebesar 28.84 mm/year. Sedangkan pada pengujian dengan penambahan inhibitor pada temperatur 30℃ sebesar 100mg laju korosi turun menjadi 0,70 mm/year dengan nilai efisiensi 97.55%. Ini merupakan efisiensi tertinggi dari semua variabel konsentrasi.
====================================================================================================================================
Corrosion is a change in material properties, especially metals due to reactions with the surrounding environment. Corrosion tends to reduce the quality of the material's mechanical properties. One way to inhibit corrosion is by adding inhibitors. Organic inhibitors are inhibitors that are considered environmentally friendly. In this study papaya leaf extract was used as an organic inhibitor. The material used is API 5L Grade B steel in 1M HCl solution as a corrosive medium with a variation temperature of 30 ℃, 40 ℃ and 50 ℃ while the concentration of extract used in this study is 0mg-1000mg. The type of testing carried out in this study is EIS (Electrochemical Impedance Spectroscopy), PDP (Potentiodynamic Polarization), weight loss and Scanning Electron Microscopy (SEM). The test results showed a decrease in the corrosion rate in API 5L Grade B steel in 1M HCl solution when added papaya leaf extract inhibitors. In the potentiodynamic polarization test the corrosion rate of the sample without inhibitors was 28.84 mm / year. While the testing with the addition of inhibitors at a temperature of 30 ℃ of 100 mg the corrosion rate dropped to 0.70 mm / year with an efficiency value of 97.55%. This is the highest efficiency of all concentration variables.

Item Type:	Thesis (Diploma)
Uncontrolled Keywords:	daun pepaya, carica papaya, inhibitor organik, API 5L, variasi temperature
Subjects:	T Technology > TN Mining engineering. Metallurgy > TN690 Metallography. Physical metallurgy
Divisions:	Faculty of Vocational > Mechanical Industrial Engineering (D4)
Depositing User:	Putri Rachmawati Hapsari
Date Deposited:	13 Aug 2026 04:04
Last Modified:	13 Aug 2026 04:04
URI:	http://repository.its.ac.id/id/eprint/69976

Actions (login required)

View Item