Pengaruh Variasi Groove Pada Bahan Baja Karbon Rendah SS400 Menggunakan Metode Pengelasan Gtaw Dengan Filler Er70s-6 Terhadap Sifat Mekanik

Priyanto, Dedi (2019) Pengaruh Variasi Groove Pada Bahan Baja Karbon Rendah SS400 Menggunakan Metode Pengelasan Gtaw Dengan Filler Er70s-6 Terhadap Sifat Mekanik. Diploma thesis, Institut Teknologi Sepuluh Nopember.

Text 10211600000046-Non_Degree.pdf Restricted to Repository staff only Download (7MB) | Request a copy

Abstract

Perkembangan ilmu pengetahuan dan teknologi tepatnya pada teknologi pengelasan dewasa ini telah banyak dipergunakan secara luas pada penyambungan batang -batang pada konstruksi bangunan baja dan konstruksi mesin. Sehingga pengetahuan mengenai teknologi pengelasan sangat diperlukan untuk mencapai kesesuaian antara hasil yang diinginkan dengan proses pengelasan yang mungkin dilakukan agar diperoleh hasil yang optimal. Dalam tugas akhir ini pengelasan yang digunakan las GTAW. Salah satu jenis sambungan las yang perlu dikaji lebih lanjut adalah sambungan las dengan groove X dan K. Pemilihan jenis groove tersebut didasarkan pada adanya kecenderungan pemakaiannya yang lebih umum. Selanjutnya untuk mengetahui kekuatan sambungan dari kedua bentuk groove dilakukan pengujian berupa tensile test, hardness test dan metallography Dari hasil pengujian tarik specimen bentuk K Groove memiliki kekuatan tarik lebih besar yaitu 495,67MPa. Sedangkan spesimen bentuk X Groove memiliki kekuatan tarik lebih rendah yaitu 486,67MPa. Berdasarkan hasil uji kekerasannya. Nilai kekerasan pada spesimen bentuk K Groove lebih besar yaitu 93,5HRB untuk spesimen bentuk X Groove memiliki nilai lebih rendah yaitu 91,3 HRB. Untuk struktur mikro hanya terdapat ferrit dan pearlit .
====================================================================================================================================
Development of challenging science and technology in today's welding technology has been widely used in connecting rods to steel building construction and machine construction. Knowledge of welding technology is needed to achieve a match between the desired results and the possible welding process in order to obtain optimal results. In this final project the welding used by GTAW welding. One type of connection that needs to be studied further is the welded joint with the X and K grooves. Furthermore, to determine the strength of the relationship of the two groove shapes by switching tensile test, hardness test, and metallography From the results of tensile testing the K Groove specimens have a greater tensile strength of 495.67 MPa. While X-shaped specimens have a lower tensile strength of 486.67 MPa. Based on the results of the failure test. The hardness value in K Groove specimens is larger, 93.5HRB for X Groove specimens having a lower value of 91.3 HRB. For microstructure only ferrite and pearlite are possessed.

Item Type:	Thesis (Diploma)
Uncontrolled Keywords:	Pengelasan, GTAW, K Groove, X Groove, tensile test, hardness test, dan metallography
Subjects:	T Technology > TS Manufactures T Technology > TS Manufactures > TS227 Welding.
Divisions:	Faculty of Vocational > Mechanical Industrial Engineering (D4)