Maryanto, Anang (2016) Pengaruh Jenis Membran Terhadap Kinerja Elektroda Pembanding Ag/Agcl. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
1409100017-Undergraduate_Thesis.pdf - Accepted Version Download (6MB) | Preview |
Abstract
Telah dibuat elektroda pembanding Ag/AgCl modifikasi yang sederhana dibandingkan dengan elektroda Ag/AgCl komersial dengan menggunakan variasi jenis membran. Membran yang digunakan berasal dari bahan yang mudah diperoleh, yaitu selulosa dari kacang hijau, poliisoprena dari lateks, grafit pensil, kaolin dari keramik ubin, dan LDPE. Kinerja dari elektroda pembanding dapat diamati dengan mengukur larutan K4[Fe(CN)6] 0,1 M.. Pengukuran larutan menggunakan sistem tiga elektroda dengan teknik voltametri. Tiga elektroda yang digunakan yaitu elektroda emas sebagai elektroda kerja, elektroda platina sebagai elektroda pembantu, dan elektroda Ag/AgCl modifikasi dan komersil sebagai elektroda pembanding. Dilakukan variasi waktu pengukuran pada setiap 2 jam selama 24 jam, tiap 24 jam selama 6 hari, tiap 3 hari selama 6 hari. Voltamogram yang diperoleh dari hasil pengukuran elektroda pembanding modifikasi dibandingkan dengan hasil pengukuran elektroda pembanding komersil menggunakan uji F an uji t untuk menentukan kinerja dari elektroda pembanding buatan sendiri. Hasil uji statistik menunjukkan elektroda modifilkasi dengan menggunakan membran poliisoprena dan LDPE memiliki kinerja yang baik. Sedangkan elektroda pembanding dengan membran selulosa, grafit, dan kaolinmemiliki kinerja yang kurang baik.
======================================================================================================
Refference electrode Ag/AgCl has been synthesized which smaller and simpler than commercial one. The electrodes were made using various membranes. The membranes were made from material that easily obtained, e.g. cellulose from mungbean, polyisoprene from tire rubber, graphite from pencil, kaolinite from ceramic tile, and LDPE. The performance of reference electrode was measured using 0.1 M K4[Fe(CN)6] solution. The measurement of the solution was using three electrode systems with voltametry method. The electrode that used were gold electrode as working electrode, platinum electrode as counter electrode, and modified Ag/AgCl electrode as reference electrode. The various measuring time were 2 hours during 24 hours, 24 hours during 6 days, 3 days during 6 days. The voltamograms of modified refrence electrode were compared with voltamograms of comercial electrode using F-test and t-test. The result shown modified reference electrode using polyisoprene and LDPE as membrane have good performance. Whereas, modified refference electrode using cellulose, graphite, and kaolinite membrane show bad performance.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Additional Information: | RSKi 660.284 24 Mar p |
| Uncontrolled Keywords: | Elektroda; voltametri; Ag/AgCl |
| Subjects: | T Technology > TP Chemical technology |
| Divisions: | Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis |
| Depositing User: | Yeni Anita Gonti |
| Date Deposited: | 04 May 2020 11:23 |
| Last Modified: | 04 May 2020 11:23 |
| URI: | http://repository.its.ac.id/id/eprint/75933 |
Actions (login required)
 |
View Item |