Rohman, M. Fatkhur (2014) Pengaruh Variasi Komposisi Serbuk Kayu Dengan Pengikat Semen Pada Pasir Cetak Terhadap Cacat Porositas Dan Kekasaran Permukaan Hasil Pengecoran Aluminium Alloy 6061. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
2111106010-Undergraduate-Thesis.pdf - Accepted Version Download (1MB) | Preview |
Abstract
Proses pengecoran dilakukan dengan cara mencairkan
logam dalam dapur pelebur, kemudian dituangkan ke dalam
cetakan dan dibiarkan membeku hingga dapat dikeluarkan dari
dalam cetakan. Metode pengecoran yang paling sering digunakan
adalah pengecoran cetakan pasir (sand casting). Faktor yang
berpengaruh terhadap kualitas hasil pengecoran cetakan pasir,
diantaranya adalah komposisi cetakan pasir dan perancangan
sistem saluran (gatting system). Penentuan komposisi cetakan
pasir dan perancangan sistem saluran harus tepat untuk
mencegah cacat yang sering terjadi dan untuk mendapatkan hasil
coran yang optimal. Salah satu komposisi utama cetakan pasir
adalah pasir cetak, pasir silika, semen, dan air, dengan bahan
penambah berupa serbuk kayu yang berfungsi untuk
meningkatkan sifat colapsability dari sebuah cetakan. Pada
penelitian ini bertujuan untuk menganalisa pengaruh variasi
komposisi serbuk kayu dengan pengikat semen pada pasir cetak
terhadap cacat porositas dan kekasaran permukaan hasil
pengecoran aluminium alloy 6061.
=================================================================================================================
Casting process is done by means of a metal melt in the
fuser kitchen, then poured into molds and allowed to set up to be
taken out of the mold. Casting method most commonly used is
sand casting. Factors that affect the quality of sand casting,
including the composition of the sand molds and designing
gatting systems. Determination of the composition of the sand
molds and designing the duct system must be appropriate to
prevent defects that often occur and to obtain optimal results
castings. One of the main composition is a sand mold molding
sand, silica sand, cement, and water, with an addition of
materials such as wood dust which serves to improve the
properties of a mold colapsability. In this study aims to analyze
the effect of variations in the composition of wood dust with
cement binder in molding sand against defects porosity and
surface roughness of an aluminum casting alloy 6061.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Uncontrolled Keywords: | Sand Casting, Aluminium Alloy 6061, Porositas, Kekasaran Permukaan |
| Subjects: | T Technology > TS Manufactures > TS233 Sand casting. Metal castings--Thermal properties. |
| Divisions: | Faculty of Industrial Technology > Mechanical Engineering > 21201-(S1) Undergraduate Thesis |
| Depositing User: | Yeni Anita Gonti |
| Date Deposited: | 17 Dec 2020 06:33 |
| Last Modified: | 17 Dec 2020 06:33 |
| URI: | http://repository.its.ac.id/id/eprint/82313 |
Actions (login required)
 |
View Item |