Rachmiananda, Rr. Indira (2021) Pengaruh Capsaicin Dari Capsicum Chinense (Cabai Habanero) Sebagai Filler Natural Antifoulant Pada Epoxy/PAA/Capsaicin Composite Untuk Coating Baja Di Air Laut. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
02511740000080-Undergraduate_Thesis.pdf - Accepted Version Download (2MB) | Preview |
Abstract
Biofouling merupakan peristiwa menempelnya organisme yang tidak diinginkan pada permukaan fasilitas laut seperti lambung kapal. Peristiwa ini dapat mengakibatkan berbagai macam dampak negatif baik di bidang ekonomi, ekologi, maupun kesehatan. Untuk mencegah terjadinya biofouling dilakukan pelapisan cat antifouling pada permukaan material. Cat antifouling mengandung biosida yang dapat mencegah menempelnya organisme fouling pada permukaan material. Namun, biosida yang digunakan sekarang beracun dan berbahaya bagi ekosistem laut. Oleh karena itu, dibutuhkan biosida yang tidak membahayakan ekosistem laut, salah satunya adalah capsaicin, senyawa yang terdapat pada cabai. Capsaicin terbukti mampu mencegah menempelnya organisme fouling pada permukaan material tanpa memberikan efek beracun. Namun, untuk memenuhi kriteria cat antifouling yang optimal, diperlukan sifat mekanik yang baik pula. Oleh karena itu, penelitian ini menganalisis pengaruh capsaicin yang diekstrak dari Capsicum chinense (cabai habanero) dalam epoxy/PAA/capsaicin composite coating dengan variasi komposisi terhadap sifat antifouling dengan perendaman pada air laut; sifat mekanik melalui pengujian lap shear strength, tensile strength, dan hardness; dan morfologi melalui pengujian stereo mikroskop. Hasil pengujian menunjukkan capsaicin mampu memberikan sifat antifouling namun menyebabkan penurunan sifat mekanik yaitu komposisi filler 0; 5; 1; dan 15wt% menghasilkan secara berurutan kekuatan tarik sebesar 9,93; 9,3; 5,42; 1,27 MPa, kekerasan sebesar 42,3; 41,3; 36,7; 23,3 HD, dan shear strength sebesar 36,12; 11,12; 8,63; dan 6,4 MPa. Oleh karena itu, komposisi filler terbaik yang dipilih adalah sebesar 5wt% karena mampu menghambat biofouling dengan tetap memiliki sifat mekanik yang tinggi.
=====================================================================================================
Biofouling is the attachment of organisms to the surface of marine facilities, such as the ship hull. These events can cause various kinds of negative impacts. Antifouling coating with biocide compounds is applied to the surface of the material to prevent biofouling. However, the biocides that are used today are harmful to marine organisms. Therefore, a biocide compound that is not harmful is needed. One of the natural compounds that have good antifouling properties is capsaicin, an active compound that comes from Capsicum sp. Capsaicin is proven to be able to prevent biofouling without giving a harmful effect. However, to meet the criteria of optimal antifouling paint, good mechanical properties are needed. Therefore, this study analyzes the effect of capsaicin extracted from Capsicum chinense in an epoxy /PAA/capsaicin composite coating with a varied composition on the antifouling properties by immersion in seawater; mechanical properties by lap shear, tensile, and hardness test; and morphology using a stereomicroscope. Capsaicin was able to give antifouling properties but also decreased the mechanical properties of the coating with 0, 5, 10, 15wt% filler which respectively resulted in tensile strength of 9,93; 9,3; 5,42; 1,27 MPa, hardness of 42,3; 41,3; 36,7; 23,3 HD, and shear strength of 36,12; 11,12; 8,63; 6,4 MPa. It can be concluded that the optimum composition of the filler for epoxy/PAA/capsaicin composite is 5wt% because it was able to give good antifouling properties while maintaining good mechanical properties.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Uncontrolled Keywords: | Antifouling, biocide, capsaicin, coating, biosida |
| Subjects: | T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL240.5 Composite materials |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | Rr. Indira Rachmiananda |
| Date Deposited: | 24 Feb 2021 09:06 |
| Last Modified: | 13 Sep 2024 06:13 |
| URI: | http://repository.its.ac.id/id/eprint/82778 |
Actions (login required)
 |
View Item |