Ramadhan, Rohim (2021) Analisa Hasil Pengelasan Kombinasi SMAW dan GMAW Pada Baja A36 Dengan Pengujian Tensile Test Dan Hardness Test. Other thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
04311640000097-Undergraduate_Theses.pdf Download (3MB) | Preview |
Abstract
Perkembangan teknologi sekarang mengalami kemajuan yang sangat pesat, terutama pada teknologi konstruksi dan bangunan bangunan lepas pantai. Proses pembuatan kontruksi kapal maupun bangunan lepas pantai tidak lepas dari proses pengelasan dan lambat laun proses pengelasan akan mengalami perkembangan . Oleh karena itu, penelitian ini bertujuan untuk mengetahui kekuatan dari uji Tarik dan kekerasan dalam suatu metode pengelasan SMAW (Shield Metal Arc Welding ), GMAW (Gas Metal Arc Welding) dan pengelasan dengan metode kombinasi SMAW dan GMAW . pengelasan kombinasi adalah proses pengelasan yang menggunakan 2 metode pengelasan pada satu join. Dalam penelitian ini yang digunakan adalah Material baja A36 yang mana merupakan salah satu material yang sering di aplikasikan untuk Kontruksi bangunan apung,bangunan lepas pantai,deck offshore ,kaki jacket ,tangki maupun pipa karena memiliki sifat yang lebih lunak dan mudah untuk dibentuk . dalam pengamatan hasil uji Tarik dapat di simpulkan bahwa hasil penglasan dengan metode kombinasi lebih tinggi dari hasil pengelasan yang lain sebesar 475,33 MPa berbanding lurus dengan uji mikro dengan hasil jumlah fase perlit pada HAZ dan weld metal lebih banyak dari hasil fase perlit lainnya. Didapatkan hasil pengujian uji kekerasan dari data yang sudah diperoleh, dapat disimpulkan bahwa nilai paling tinggi terdapat pada pengelasan GMAW. Ini dikarenakan memiliki kualitas deposit logam yang tinggi.
=====================================================================================================
Echnological developments are now experiencing very rapid advances, especially in construction technology and offshore building buildings. The process of making ship construction and offshore buildings cannot be separated from the welding process and gradually the welding process will experience development therefore, this study aims to determine the strength of the tensile and hardness test in a welding method of SMAW (Shield Metal Arc Welding), GMAW (Gas Metal Arc Welding) and welding using a combination of SMAW and GMAW methods. Combined welding is a welding process that uses 2 welding methods on one joint. In this study, the A36 steel material is used which is one of the materials that is often applied for floating building construction, offshore buildings, offshore decks, jacket legs, tanks and pipes because it has properties that are softer and easier to shape. In observing the results of the tensile test, it can be concluded that the welding results with the combination method are higher than the other welding results of 475.33 MPa which is directly proportional to the micro test with the results of the number of pearlite phases in HAZ and weld metal being higher than the results of other pearlite phases. The hardness test results obtained from the data that have been obtained, it can be concluded that the highest value is found in GMAW welding. This is because it has a high quality metal deposit.
| Item Type: | Thesis (Other) |
|---|---|
| Uncontrolled Keywords: | Baja A36, Shield Metal Arc Welding, Gas Metal Arc Welding, Pengelasan metode kombinasi SMAW dan GMAW |
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) > TA418.16 Materials--Testing. T Technology > TK Electrical engineering. Electronics Nuclear engineering > TK4660 Welding; Electric welding. T Technology > TS Manufactures > TS227 Welding. |
| Divisions: | Faculty of Marine Technology (MARTECH) > Ocean Engineering > 38201-(S1) Undergraduate Thesis |
| Depositing User: | Rohim Ramadhan |
| Date Deposited: | 26 Feb 2021 06:04 |
| Last Modified: | 08 Jul 2024 15:29 |
| URI: | http://repository.its.ac.id/id/eprint/82909 |
Actions (login required)
 |
View Item |