Perbandingan Laju Korosi Substrat Baja Karbon St41 Dengan Pelapis Bahan Titanium Nitride Dengan Ss 316l Untuk Bahan Implan Tulang

Mauluddin, Yasmi (2021) Perbandingan Laju Korosi Substrat Baja Karbon St41 Dengan Pelapis Bahan Titanium Nitride Dengan Ss 316l Untuk Bahan Implan Tulang. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

Text 10211600000094_Non_Korosi Implan Tulang.pdf - Accepted Version Restricted to Repository staff only Download (5MB) | Request a copy

Abstract

Salah satu jenis bahan yang biasa digunakan dalam pembuatan alat-alat implan tulang adalah SS 316L. Dalam penerapannya SS 316L terbilang mahal. Untuk mendapatkan harga yang lebih terjangkau maka pada bahan dasar pembuatannya dilakukan pergantian, dengan resiko ketahanan yang berbeda. Untuk mengetahui ketahanan korosi dengan bahan yang berbeda maka dilakukan penelitian ini.Dalam penelitian ini material yang digunakan adalah baja ST41 yang dilapisi oleh titanium nitride dalam larutan Simulated Body Fluid sebagai media korosif dan dilakukan perbandingan dengan SS 316L. Jenis pengujian yang dilakukan pada penelitian kali ini adalah Polarisasi potensiodinamik dengan metode tafel dan weight loss.Hasil pengujian menunjukkan adanya penurunan laju korosi yang signifikan pada baja ST41 yang dilapisi dengan titanium nitride dalam larutan SBF ketika telah dilakukan proses perendaman selama 7 hari. Pada pengujian Polarisasi Potensiodinamik laju korosi pada hari ke 7 adalah 4,0902 x 10-4 mm/year untuk pelapis TiN dan 5,2665 x 10-3 mm/year untuk SS 316L. Maka laju korosi ST41 pelapis TiN setelah melewati 7 hari perendaman lebih rendah dibandingkan SS 316L.
====================================================================================================
One type of material commonly used in making bone implant devices is SS 316L. In its applications SS 316L is quite expensive. In order to get a more affordable price, the basic materials are changed but with different resistance. To find out the corrosion resistance with different materials, this study was conducted.In this study the material used was ST41 coated with titanium nitride in a Simulated Body Fluid solution as a corrosive medium and do a comparison of the corrosion rate with SS 316L. The type of test in this study was potentiodynamic polarization with the tafel method and weight loss.The test results showed a significant reduction of corrosion rate in ST41 coated with Titanium Nitride in SBF solution when the immersion process was carried out for 7 days. In the Potentiodynamic Polarization test the corrosion rate on day 7 was 4,0902 x 10-4 mm/year for TiN coatings and 5.2665x10-3 mm/year for SS 316L. So the corrosion rate of ST41 with TiN coating after passing 7 days of immersion is lower than SS 316L.

Item Type:	Thesis (Undergraduate)
Uncontrolled Keywords:	Kata kunci : Laju Korosi, ST41, SS 316L, Titanium Nitride, SBF, Implan Tulang Key Word : ST 41 Steel, Corrosion Rate, SBF, Titanium Nitride, Potentiodynamic Polarization, Weight Loss, Bone Implant
Subjects:	T Technology > TJ Mechanical engineering and machinery T Technology > TJ Mechanical engineering and machinery > TJ1186.B5 Metal-cutting tools--Design and construction.
Divisions:	Faculty of Vocational > Mechanical Industrial Engineering (D4)
Depositing User:	Yasmi Mauluddin
Date Deposited:	09 Mar 2021 07:30
Last Modified:	09 Mar 2021 07:30
URI:	http://repository.its.ac.id/id/eprint/83854

Actions (login required)

View Item