Polimer Elektrolit Padat PEO/NaClO4 dengan Nano-SiO2 dari Ampas Tebu sebagai Filler pada Baterai Natrium Ion

Muhaiminah, Zakkiyyah Hidayatul (2021) Polimer Elektrolit Padat PEO/NaClO4 dengan Nano-SiO2 dari Ampas Tebu sebagai Filler pada Baterai Natrium Ion. Masters thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 01221750012007-Master_Thesis.pdf] Text
01221750012007-Master_Thesis.pdf - Accepted Version
Restricted to Repository staff only until 1 April 2023.

Download (2MB) | Request a copy

Abstract

Polimer elektrolit padat telah banyak digunakan dalam baterai natrium ion karena mempunyai karakteristik yang unik, seperti tidak adanya kebocoran, stabilitas elektrokimia yang bagus, fleksibilitas dan plastisitas yang baik serta stabil pada temperatur tinggi. Polyethylene Oxide (PEO) merupakan polimer yang mempunyai stabilitas elektrokimia yang tinggi, fleksibilitas dan plastisitas yang baik sehingga cocok digunakan untuk polimer elektrolit padat. Polimer elektrolit padat PEO sendiri masih mempunyai konduktivitas yang cukup rendah yaitu 10-6-10-8 S/cm untuk digunakan dalam baterai natrium ion, sehingga dibutuhkan beberapa modifikasi untuk menambah konduktivitasnya. Penambahan garam NaClO4 dilakukan sebagai sumber ion natrium dan plastisizer, sedangkan penambahan nano-SiO2 sebagai filler dilakukan untuk megurangi kristalinitas serta menambah konduktivitas polimer elektrolit padat. Nano-SiO2 diperoleh dari sintesis ampas tebu menggunakan metode sol-gel. Polimer elektrolit padat PEO/NaClO4 dengan penambahan nano-SiO2 dari ampas tebu sebanyak 5% pada suhu 60oC menunjukkan konduktivitas ion tertinggi yaitu sebesar 1,18 x 10-6 S/cm. Adanya filler membuktikan bahwa terjadi kenaikan konduktifitas ion dan stabilitas antarmuka yang baik dengan elektroda. Dengan demikian, elektrolit padat merupakan elektrolit yang menjanjikan untuk aplikasi pada baterai natrium ion.
=====================================================================================================
Solid polymer electrolyte has been widely used in sodium ion batteries because it has unique characteristics, such as the absence of leakage, good electrochemical stability, flexibility and good plasticity, also stable at high temperatures. Polyethylene Oxide (PEO) is a polymer that has high electrochemical stability, flexibility and good plasticity make it suitable to use in solid polymer electrolyte. The solid polymer electrolyte PEO itself still has a fairly low conductivity, of 10-6-10-8 S/cm to be used in sodium ion batteries, so some modifications are needed to increase the conductivity. The addition of NaClO4 is done as sodium ion source and plastisizer, while the addition of nano-SiO2 as a filler is done to reduce the crystallinity also increase the conductivity. Nano-SiO2 was obtained from bagasse ash synthesis using sol-gel method. Solid polymer electrolite PEO/NaClO4 with addition of nano-SiO2 from bagasse ash 5% at 60oC showed the highest ionic conductivity 1,18 x 10-6 S/cm. The filler presence proves that there is an increase ion conductivity and good interface stability with the electrodes. Thus, solid polymer electrolytes are promising electrolytes for applying in sodium ion batteries.

Item Type: Thesis (Masters)
Uncontrolled Keywords: polimer elektrolit padat, PEO, NaClO4, SiO2, baterai natrium ion, solid polymer electrolyte, PEO, NaClO4, SiO2, sodium ion battery
Subjects: T Technology > TK Electrical engineering. Electronics Nuclear engineering > TK2941 Storage batteries
T Technology > TP Chemical technology > TP1140 Polymers
Divisions: Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47101-(S2) Master Thesis
Depositing User: Zakkiyyah Hidayatul Muhaiminah
Date Deposited: 09 Mar 2021 21:07
Last Modified: 09 Mar 2021 21:07
URI: http://repository.its.ac.id/id/eprint/83909

Actions (login required)

View Item View Item