Analisis Pengaruh Jenis Dan Komposisi Serbuk Arang (Tempurung Kelapa Dan Kayu Jati) Serta Penambahan Clay (Lumpur Lapindo) Terhadap Karakteristik Briket Komposit Sekam Padi (Briko-Sp)

Rosmawati, Siregar (2021) Analisis Pengaruh Jenis Dan Komposisi Serbuk Arang (Tempurung Kelapa Dan Kayu Jati) Serta Penambahan Clay (Lumpur Lapindo) Terhadap Karakteristik Briket Komposit Sekam Padi (Briko-Sp). Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 02511950015004_197801132002121003-Master_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2023. Download (2MB) | Request a copy

Abstract

Briket merupakan salah satu bahan bakar yang berasal dari biomassa. Biomassa yang digunakan dalam penelitian ini adalah sekam padi, Tempurung Kelapa dan serbuk kayu jati. penelitian ini bertujuan untuk mengetahui pengaruh variasi komposisi arang sekam padi, arang tempurung kelapa dan arang serbuk kayu jati dengan bahan perekat dan bahan aditif lumpur lapindo (RHP/TWP/CH) terhadap parameter fisis, kimia dan laju pembakaran. Parameter yang diinvestigasi dari briket yang dibuat adalah densitas, kadar air kadar abu, zat terbang (volatile matter), karbon terikat (fixed carbon), nilai kalor dan laju pembakaran. Nilai densitas yang diperolah pada pengujian briket arang sekam padi, arang tempurung kelapa dan arang serbuk kayu jati dengan perekat dan lumpur lapindo dengan komposisi (RHP/TWP/CH) adalah ( 0,8 - 1,12 g/cm3 ). Briket terbaik dengan komposisi (RHP/TWP/CH) dimana nilai kadar air adalah 4,25 - 6, 94 % dan nilai kalor mencapai nilai 6367,5 - 10747,5 %. Hasil ini sesuai dengan sesuai standarisasi SNI No. 1-6235-2000. Briket dengan komposisi (RHP/CH/Clay 20%) memiliki laju memiliki nilai terendah yang diperoleh sebesar 0,003 gram/menit laju pembekaran tertinggi yang didapatkan sebesar 0,020 gram/menit dengan komposisi (RHP/TWP 35%).

================================================================================================

Briquette is one of the fuels derived from biomass. The biomass used in this research is rice husk, coconut shell, and teak wood powder. This study aims to determine the effect of variations in the composition of rice husk charcoal, coconut shell charcoal, and teak wood powder charcoal with adhesives and Lapindo mud additives (RHP/TWP/CH) on physical, chemical, and combustion parameters. The investigated parameters of the briquettes made were density, moisture content, ash content, volatile matter, fixed carbon, calorific value, and combustion rate. The density values obtained in the testing of rice husk charcoal briquettes, coconut shell charcoal, and teak wood powder charcoal with adhesive and lapindo mud with the composition (RHP/TWP/CH) were ( 0.8 - 1.12 g/cm3 ). The best briquettes with composition (RHP/TWP/CH) where the water content value is 4.25 - 6, 94% and the calorific value reaches 6367.5 - 10747.5 %. This result is under the standardization of SNI No. 1-6235-2000. Briquettes with the composition (RHP/CH/Clay 20%) had the lowest rate of 0.003 grams/minute, the highest rate of combustion was 0.020 grams/minute with the composition (RHP/TWP 35%).

Item Type:	Thesis (Masters)
Uncontrolled Keywords:	Briquettes, Rice Husk Charcoal, Coconut Shell Charcoal, Teak Wood Charcoal Briket, Arang Sekam Padi, Arang Tempurung Kelapa, Arang Kayu Jati
Subjects:	Q Science > QC Physics > QC173.4.C63 Composite materials T Technology > TA Engineering (General). Civil engineering (General)
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Rosmawati Siregar
Date Deposited:	14 Aug 2021 07:37
Last Modified:	14 Aug 2021 07:37
URI:	http://repository.its.ac.id/id/eprint/86389