Peningkatan Tegangan Breakdown Isolasi Minyak Yang Dimodifikasi Menggunakan Konduktif Nanopartikel

Siahaan, Violyn Yulistika (2021) Peningkatan Tegangan Breakdown Isolasi Minyak Yang Dimodifikasi Menggunakan Konduktif Nanopartikel. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

Text 07111740000149-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2023. Download (3MB) | Request a copy

Abstract

Nanofluida Fe3O4 merupakan nanofluid magnetik yang mengandung partikel konduktif berukuran nanometer. Saat ini, berkembang penelitian mengenai minyak transformator yang dimodifikasi dengan nanopartikel yang disebut dengan nanofluid, dapat digunakan sebagai insulasi cairan pada transformator. Studi ini menggunakan pembangkitan tegangan tinggi AC dengan jenis elektroda setengah bola sesuai standar IEC 60156. Minyak yang digunakan pada studi ini yaitu minyak mineral Shell Diala B dan terdapat 5 variasi konsentrasi konduktif nanopartikel (Fe3O4) yang berbeda. Pada studi ini memiliki 2 metode pre-kondisi yaitu minyak mineral dikeringkan menggunakan metode konvensional dan metode menggunakan vacuum oven. Penelitian ini juga melewati proses sedimentasi dengan kondisi nanofluid yang didiamkan selama 1 hari dan 7 hari dan adanya penambahan surfaktan pada larutan nanofluid agar larutan nanopartikel tidak menggumpal dan terdispersi dengan baik.
Adapun hasil pengujian yang didapatkan bahwa nanofluid memiliki nilai tegangan breakdown dielektrik yang lebih tinggi (dua kali) daripada minyak mineral. Begitu pula untuk metode mengggunakan vacuum oven memiliki nilai lebih tinggi daripada metode konvensional pada saat konsentrasi nanopartikel 0,003% sedangkan nilai optimal pada metode konvensional saat konsentrasi nanopartikel 0,008%. Pada penelitian ini semakin banyak jumlah konsentrasi konduktif nanopartikel yang dipakai maka semakin kecil pula nilai pada breakdown voltage. Penambahan surfaktan juga mempengaruhi kekuatan dielektrik pada nanofluid, adanya penambahan surfaktan maka nilai breakdown voltage semakin meningkat.
================================================================================================
Nanofluid Fe3O4 is a magnetic nanofluid containing nanometer-sized conductive particles. Currently, research is developing on transformer oil modified with nanoparticles called nanofluid, which can be used as liquid insulation in transformers. This study uses high voltage AC generator with hemispherical electrode type according to IEC 60156 standard. The oil used in this study is Shell Diala B mineral oil and there are 5 different concentrations of conductive nanoparticles (Fe3O4). In this study, there are 2 pre-conditioning methods, namely mineral oil dried using a conventional method and a method using a vacuum oven. This study also went through a sedimentation process with nanofluid conditions that were left for 1 day and 7 days and the addition of surfactants to the nanofluid solution so that the nanoparticle solution did not agglomerate and was well dispersed.
The test results showed that nanofluid has a higher dielectric breakdown voltage (twice) than mineral oil. Likewise, the method using a vacuum oven has a higher value than the conventional method when the nanoparticle concentration is 0.003%, while the optimal value for the conventional method is when the nanoparticle concentration is 0.008%. In this study, the higher the concentration of conductive nanoparticles used, the smaller the breakdown voltage value. The addition of surfactants also affects the dielectric strength of the nanofluid, the addition of surfactants will increase the breakdown voltage value.

Item Type:	Thesis (Undergraduate)
Uncontrolled Keywords:	Conductive Nanoparticles (Fe3O4), Transformer Insulating Oil, Nanofluids, AC Breakdown Voltage, Konduktif Nanopartikel (Fe3O4), Minyak Isolasi Transformator, Nanofluida, AC Breakdown Voltage
Subjects:	T Technology > TK Electrical engineering. Electronics Nuclear engineering > TK3401 Insulation and insulating materials
Divisions:	Faculty of Intelligent Electrical and Informatics Technology (ELECTICS) > Electrical Engineering > 20201-(S1) Undergraduate Thesis
Depositing User:	Violyn Yulistika Siahaan
Date Deposited:	15 Aug 2021 03:06
Last Modified:	15 Aug 2021 03:06
URI:	http://repository.its.ac.id/id/eprint/86718

Actions (login required)

View Item