Diakana, Achmad Ridwan (2021) Impregnasi ZnO Pada Ampas Tebu Termodifikasi CTAB dan Aplikasinya Untuk Menghilangkan Zat Warna Metil Jingga. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Text
01211740000043-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2023. Download (2MB) | Request a copy |
Abstract
Seng Oksida (ZnO) merupakan semikonduktor yang dapat digunakan sebagai katalis dalam proses fotokatalitik zat warna. Beberapa penelitian menunjukkan kurang optimalnya ZnO dalam aktivitas fotokatalitik untuk zat warna anionik. Kemampuan fotokatalitik ZnO yang kurang baik terhadap zat warna anionik dapat ditingkatkan dengan penambahan material pendukung. Ampas tebu merupakan salah satu limbah lingkungan yang dapat dimanfaatkan sebagai material pendukung, tetapi kemampuan ampas tebu masih belum maksimal dalam penyerapan zat warna sehingga perlu dilakukan modifikasi. Pada penelitian ini dilakukan modifikasi ampas tebu dengan menambahkan surfaktan cetyl trimethylammonium bromide (CTAB) sebagai material pendukung untuk fotokatalitik ZnO. Impregnasi ZnO pada ampas tebu termodifikasi (ATM) memiliki variasi massa sebesar 5, 10, dan 20%. Pengujian ZnO/ampas tebu termodifikasi (ZnO/ATM) pada metil jingga dilakukan dengan variasi waktu ( 1, 2, 3, 4, dan 5 jam). Hasil penelitian yang telah dilakukan didapatkan hasil yang optimal pada ZnO/ATM 10% dengan persen pengurangan pada proses fotokatalitik sebesar 55,36% dan adsorpsi 36,49% dalam waktu 5 jam. Peningkatan persen pengurangan pada ZnO/ATM dapat dilakukan dengan penambahan H2O2 dalam proses reaksi. Hasil penambahan tersebut meningkatkan persen pengurangan menjadi 72,98% (fotokatalitik) dan 54,4% (adsorpsi).
======================================================================================================
Zinc Oxide (ZnO) is a semiconductor that can be used as a catalyst in the photocatalytic process of dyes. Several studies have shown that ZnO is less than optimal in photocatalytic activity for anionic dyestuffs. The less of photocatalytic ability of ZnO against anionic dyes can be improved by adding a support material. Bagasse is one of the environmental wastes that can be used as a supporting material, but the ability of bagasse is still not maximized in the absorption of dyes so it needs to be modified. In this study, sugarcane bagasse was modified by adding surfactant cetyl trimethylammonium bromide (CTAB) as a support material for ZnO photocatalytic. ZnO impregnation on modified bagasse (ATM) had mass variations of 5, 10, and 20%. Testing of ZnO/modified bagasse (ZnO/ATM) on methyl orange was carried out with time variations (1, 2, 3, 4, and 5 hours). The results of the research that have been carried out have obtained optimal results at 10% ZnO/ATM with a percent reduction in the photocatalytic process of 55.36% and 36.49% adsorption within 5 hours. The increase in the percent reduction in ZnO/ATM can be done by adding H2O2 in the reaction process. The results of the addition increased the percent reduction to 72.98% (photocatalytic) and 54.4% (adsorption).
Item Type: | Thesis (Undergraduate) |
---|---|
Uncontrolled Keywords: | Fotokatalitik, Adsorpsi, ZnO, Ampas Tebu, dan Metil Jingga |
Subjects: | Q Science Q Science > QD Chemistry Q Science > QD Chemistry > QD716 Photocatalysis. |
Divisions: | Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47201-(S1) Undergraduate Thesis |
Depositing User: | Achmad Ridwan Diakana |
Date Deposited: | 24 Aug 2021 06:48 |
Last Modified: | 24 Aug 2021 06:48 |
URI: | http://repository.its.ac.id/id/eprint/90074 |
Actions (login required)
View Item |