Analisis Pengaruh 10-Methacryloyloxydecyl Dihydrogen Phosphate Sebagai Coupling Agent Terhadap Morfologi dan Sifat Mekanik Al2O3/ZrSiO4 Untuk Aplikasi Implan Mahkota Gigi

Febriani, Feby Alindi (2022) Analisis Pengaruh 10-Methacryloyloxydecyl Dihydrogen Phosphate Sebagai Coupling Agent Terhadap Morfologi dan Sifat Mekanik Al2O3/ZrSiO4 Untuk Aplikasi Implan Mahkota Gigi. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

Text 02511840000133-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 April 2024. Download (4MB) | Request a copy

Abstract

Dalam bidang biomedis, komposit telah banyak digunakan sebagai material implan gigi. Material komposit yang biasa digunakan sebagai implan gigi salah satunya adalah komposit Al2O3/ZrO2. Penelitian ini memanfaatkan Al2O3/ZrSiO4 yang akan dimodifikasi menggunakan coupling agent 10-MDP. Variasi yang digunakan adalah persentase penambahan 10-MDP sebanyak 0, 1, 3, dan 5 wt% serta komposisi Al2O3/ZrSiO4 sebesar 80:20, 85:15, dan 90:10. Penelitian ini menunjukkan bahwa penambahan 10-MDP dapat meningkatkan adhesi pada interface komposit dan mempengaruhi sifat mekanik komposit Al2O3/ZrSiO4. Semakin besar persentase penambahan 10-MDP pada komposit Al2O3/ZrSiO4, semakin rekat pula interface pada komposit. Penambahan persentase 10-MDP juga meningkatkan nilai kekerasannya dari 8.75 GPa hingga 10.85 GPa. Sedangkan untuk kekuatan tekan, penambahan 1, 3, dan 5 wt% 10-MDP belum cukup untuk meningkatkan nilai kuat tekan pada komposit Al2O3/ZrSiO4, walaupun seiring bertambahnya persentase 10-MDP, kuat tekannya semakin meningkat yaitu dari 30.37 MPa hingga 45.23 MPa. Untuk pengaruhnya terhadap temperatur, penambahan 10-MDP tidak dapat memperbaiki sifat termal komposit, karena seiring bertambahnya persentase 10-MDP, persentase penurunan massanya semakin banyak.
================================================================================================
In biomedic application, composite has been used for dental implant. Composite that usually used for dental implant is Al2O3/ZrO2. This research uses Al2O3/ZrSiO4 which modified using 10-MDP coupling agent. Variation that used in this research are percentage of 10-MDP as 0, 1, 3, and 5 wt% and Al2O3/ZrSiO4 composition as 80:20, 85:15, and 90:10. This research shows that addition of 10-MDP can increase adhesion of composite interface and affect mechanical properties of Al2O3/ZrSiO4. Increasing 10-MDP percentage on Al2O3/ZrSiO4 will improve the adhesion of composite interface. Addition of 10-MDP percentage also increases the hardness value from 8.75 GPa to 10.85 GPa. But, addition of 1, 3, and 5 wt% 10-MDP was not sufficient to increase compressive strength of the composite, although as the percentage of 10-MDP increases, the compressive strength increases from 30.37 MPa to 45.23 MPa. For its effect on temperature, addition of 10-MDP cannot improve the thermal properties, because as the percentage of 10-MDP increases, the percentage of mass loss is increasing.

Item Type:	Thesis (Undergraduate)
Uncontrolled Keywords:	10-MDP, Alumina, Coupling Agent, Dental Implant, Zircon, 10-MDP, Coupling Agent, Implan Gigi, Zirkon
Subjects:	Q Science > QC Physics > QC173.4.C63 Composite materials
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Feby Alindi Febriani
Date Deposited:	04 Feb 2022 02:03
Last Modified:	04 Feb 2022 02:03
URI:	http://repository.its.ac.id/id/eprint/92782