Desain Alat Uji Efisiensi Anoda Korban Sesuai Standar DnVGL-RPB401 untuk Paduan Aluminium dengan Variasi Volume Elektrolit

Rennu, Farah Zhafirah (2022) Desain Alat Uji Efisiensi Anoda Korban Sesuai Standar DnVGL-RPB401 untuk Paduan Aluminium dengan Variasi Volume Elektrolit. Other thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 02511840000102-Undergraduate_Thesis.pdf]
Preview
Text
02511840000102-Undergraduate_Thesis.pdf - Accepted Version

Download (2MB) | Preview

Abstract

Korosi adalah sebuah fenomena natural yang bersifat destruktif, berbahaya, dan menyebabkan kerugian besar. Salah satu metode pencegahan korosi adalah proteksi katodik dengan menggunakan anoda korban. Salah satu standar praktik yang digunakan untuk mendesain proteksi katodik ini adalah DnVGL-RPB401. Efisiensi dari anoda dapat diketahui dengan melakukan pengujian DnVGL-RPB401. Penelitian ini dilakukan untuk membuat alat uji efisiensi anoda korban dengan standar DnVGL-RPB401. Pada penelitian ini, uji kelayakan dilakukan menggunakan variasi volume elektrolit, yaitu 7 liter, 10 liter, dan 15 liter. Hasil efisiensi yang didapatkan untuk volume 7, 10, dan 15 liter adalah 96.595%, 94.468%, dan 92.694% untuk anoda Al-ICS dan 87.855%, 80.559%, 70.774% untuk anoda Al-Lab Korosi. Hasil pengujian dari rangkaian yang dirancang ulang mendekati alat uji pada PT. Indocast Fransasia Sejahtera.
====================================================================================================
Corrosion is a natural phenomenon that is destructive, dangerous, and causes great losses. One of the corrosion prevention methods is cathodic protection using a sacrificial anode. One of the standard practices used to design this cathodic protection is DnVGL-RPB401. The efficiency of the anode can be determined by testing the DnVGL-RPB401. This research was conducted to make a sacrificial anode efficiency test kit with the DnVGL-RPB401 standard. In this research, the test was carried out using Aluminum as anode and using variations in electrolyte volume, namely 7 liters, 10 liters, and 15 liters. The efficiency results obtained for volume 7, 10, and 15 liters were 96.595%, 94.468%, and 92.694% for the Al-ICS anode and 87.855%, 80.559%, 70.774% for the Corrosion Al-Lab anode. The test results of the redesigned circuit approach the test equipment at PT. Indocast Fransasia Sejahtera

Item Type: Thesis (Other)
Uncontrolled Keywords: Aluminum, DnVGL-RPB 401, Efficiency, Volume
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA462 Metal Corrosion and protection against corrosion
T Technology > TA Engineering (General). Civil engineering (General) > TA467 Iron and Steel Corrosion and protection against corrosion
Divisions: Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Farah Zhafirah Rennu
Date Deposited: 04 Feb 2022 07:48
Last Modified: 04 Jul 2024 06:48
URI: http://repository.its.ac.id/id/eprint/92794

Actions (login required)

View Item View Item