Pengaruh Variasi Temperatur Sintering Terhadap Sifat Mekanik Dan Struktur Mikro Pada Campuran Serbuk Logam Sisa Pemesinan Dengan Metode Metalurgi Serbuk

Falnanda, Muhammad Bintang (2022) Pengaruh Variasi Temperatur Sintering Terhadap Sifat Mekanik Dan Struktur Mikro Pada Campuran Serbuk Logam Sisa Pemesinan Dengan Metode Metalurgi Serbuk. Other thesis, Institut Teknologi Sepuluh Nopember Surabaya.

Text 10211810000059-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 September 2024. Download (4MB) | Request a copy

Abstract

Dalam pembuatan produk pada proses pemesinan tentu akan menghasilkan hasil samping berupa limbah sisa yang belum dapat diolah kembali lebih maksimal, seperti serbuk sisa pemesinan. Untuk mengurangi jumlah limbah yang dihasilkan, serbuk sisa pemesinan dapat diolah kembali. Penelitian ini bertujuan untuk mengetahui komposisi kandungan bahan pada serbuk sisa pemesinan, mengetahui cara merancang punch dan die untuk mengeluarkan spesimen setelah dikompaksi, dan untuk mengetahui pengaruh variasi temperatur sintering terhadap microstructure dan sifat mekanik spesimen. Penelitian ini menggunakan metode Metalurgi Serbuk. Sebelum diolah, serbuk sisa akan diuji XRF terlebih dahulu untuk mengetahui kandungan dan komposisi logam yang terdapat di dalam serbuk sisa pemesinan tersebut. Setelah itu, dilakukan perncangan punch dan die untuk membentuk spesimen berukuran diameter 20mm dan panjang 20mm dan dilakukan kompaksi dengan tekanan 400 MPa. Kemudian dilakukan proses sintering dengan variabel temperatur 1000oC, 1100oC, dan 1200oC. Setelah proses metalurgi serbuk telah selesai dilakukan beberapa pengujian. Dari penelitian ini spesimen dengan temperatur sintering 1200oC memiliki nilai hasil pengujian yang lebih baik dari pada temperatur sintering 1000 oC dan 1100oC. Hal ini dapat terjadi dikarenakan, temperatur sintering sangat mempengaruhi struktur mikro maupun sifat mekanik dari hasil produk metalurgi serbuk. Pada pengujian kekerasan, geser dan porositas semakin tinggi temperatur sintering maka nilai yang dihasilkan dari pengujian tersebut juga meningkat. Peningkatan ini disebabkan karena semakin tinggi temperatur sintering maka struktur mikro yang terbentuk cenderung ferrit yang memiliki sifat mekanik lunak dan ulet
======================================================================================================================================
In the manufacture of products in the machining process, of course, it will produce by-products in the form of residual waste that cannot be reprocessed more optimally, such as machining waste powder. To reduce the amount of waste generated, the remaining powder from machining can be reprocessed. This study aims to determine the composition of the material content of the remaining machining powder, to determine how to design punch and die to remove the spesimen after compaction, and to determine the effect of variations in sintering temperatur on the microstructure and mechanical properties of the spesimen. This research uses Powder Metallurgy method. Before being processed, the remaining powder will be tested by XRF first to determine the content and composition of the metal contained in the remaining machining powder. After that, the punch and die were designed to form a spesimen measuring 20mm in diameter and 20mm in length and compacted with a pressure of 400 MPa. Then the sintering process was carried out with temperatur variables of 1000oC, 1100oC, and 1200oC. After the powder metallurgical process has been completed, several tests are carried out. From this study, specimens with a sintering temperature of 1200oC had better test results than the sintering temperatures of 1000oC and 1100oC. This can happen because the sintering temperature greatly affects the microstructure and mechanical properties of the powder metallurgical products. In the test of hardness, shear and porosity, the higher the sintering temperature, the value resulting from the test also increases. This increase is due to the higher sintering temperature, the microstructure formed tends to be ferrite which has soft and ductile mechanical properties

Item Type:	Thesis (Other)
Additional Information:	RSMI 671.37 Fal p-1
Uncontrolled Keywords:	Sisa Pemesinan, Metalurgi Serbuk, Kompaksi, Sintering
Subjects:	T Technology > TS Manufactures > TS320 Steel--Metallurgy.
Divisions:	Faculty of Vocational > Mechanical Industrial Engineering (D4)
Depositing User:	EKO BUDI RAHARJO
Date Deposited:	21 Dec 2022 06:58
Last Modified:	21 Dec 2022 06:58
URI:	http://repository.its.ac.id/id/eprint/95261