Uji Lapangan Untuk Mempelajari Pengaruh Orientasi Weld Overlay Terhadap Laju Erosi Plat yang Digunakan pada Mill Batubara Pembangkit Listrik

Nugroho, Dimas Satrio (2023) Uji Lapangan Untuk Mempelajari Pengaruh Orientasi Weld Overlay Terhadap Laju Erosi Plat yang Digunakan pada Mill Batubara Pembangkit Listrik. Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 6007201036-Master_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 April 2025. Download (6MB) | Request a copy

Abstract

Penelitian ini menyelidiki pengaruh orientasi weld overlay plat mill batubara pada pembangkit listrik. Karakteristik dari mill batubara menghasilkan aliran udara primer yang terkonsentrasi pada titik tertentu sehingga keausan yang terjadi pada plat mill tidak merata. Hal ini dibuktikan pada saat internal check mill ditemukan terdapat area dinding dan manhole mill dengan tingkat keausan yang lebih cepat dari area yang lain, sehingga beberapa kali terjadi plat mill berlubang pada area tersebut. Kondisi ini dapat membahayakan pengoperasian dan mempengaruhi keandalan mill. Ada dua spesimen yang dibuat, untuk spesimen 1 weld overlay diproses dengan cara submerged arc welding dan spesimen 2 diproses dengan cara flux core arc welding. Setiap spesimen dibuat 4 orientasi las sudut 0, 45, 90 dan 135. Kemudian metode pengujian yang digunakan adalah pengujian langsung, benda uji dipasang pada sisi manhole yang terindikasi mempunyai keausan paling cepat dengan lama pengujian 720 jam. Hasil penelitian menunjukan ketebalan spesimen setelah diuji didalam mill dibandingkan dengan ketebalan sebelum diuji. Hasil pengukuran orientasi plat setelah diuji terhadap waktu pengujian adalah laju erosi. laju erosi pada weld overlay yang diproses dengan submerged arc welding untuk sudut 0 adalah 253.043 mm3/tahun, untuk sudut 45 adalah 240.769 mm3/tahun, untuk sudut 90 adalah 307.806 mm3/tahun dan untuk sudut 135 adalah 237.936 mm3/tahun. Kemudian untuk weld overlay yang diproses dengan flux core arc welding untuk sudut 0 adalah , untuk sudut 45 adalah , untuk sudut 90 adalah dan untuk sudut 135 adalah . sehingga laju erosi terendah terjadi pada kedua spesimen pada orientasi sudut 135. Orientasi sudut 135 pada proses flux core arc welding mempunyai laju erosi yang paling kecil.
==================================================================================================
This study investigates the influence of the weld overlay orientation of coal mill plates in power plants. The characteristics of the coal mill produce primary airflow that is concentrated at a certain point so that the wear that occurs on the mill plate is uneven. This is evidenced during the internal check of the mill, it was found that there were areas of the mill wall and manhole with a faster erosion rate than other areas, so several times there were mill plates with holes in these areas. This condition can jeopardize the operation and affect the reliability of the mill. There are two specimens made, for specimen 1 weld overlay processed by submerged arc welding and specimen 2 processed by flux core arc welding. Each specimen is made of 4 angle weld orientations 0, 45, 90, and 135. Then the test method used is direct testing, the test object is mounted on the side of the manhole which is indicated to have the fastest wear with a test duration of 720 hours. The results showed the thickness of the specimen after being tested in the mill compared to the thickness before being tested. The erosion rate of the weld overlay processed with submerged arc welding for the angle 0 is 253,043 mm3/year, for the angle 45 is 240,769 mm3/year, for the angle 90 is 307,806 mm3/year and for the angle 135 is 237,936 mm3/year. Then for the weld overlay processed with flux core arc welding for angle 0 is, for angle 45 is, for angle 90 is and for angle 135 is. so that the lowest erosion rate occurs in both specimens at angle orientation 135. The angle orientation 135 in the flux core arc welding process has the smallest erosion rate.

Item Type:	Thesis (Masters)
Uncontrolled Keywords:	Plat aus, mill, orientasi weld overlay, laju erosi, tahan aus, Wearplate, weld overlay orientation, erosion rate, wear resistant
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA418.16 Materials--Testing.
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Mechanical Engineering > 21101-(S2) Master Thesis
Depositing User:	Dimas Satrio Nugroho
Date Deposited:	17 Feb 2023 14:54
Last Modified:	17 Feb 2023 14:54
URI:	http://repository.its.ac.id/id/eprint/97622

Actions (login required)

View Item