Pengaruh pH dan Konsentrasi Green Inhibitor Ekstrak Bunga Cengkeh (Syzygium Aromaticum) Terhadap Korosivitas Baja API 5L Grade B

Salsadillah, Suli Rahayu (2023) Pengaruh pH dan Konsentrasi Green Inhibitor Ekstrak Bunga Cengkeh (Syzygium Aromaticum) Terhadap Korosivitas Baja API 5L Grade B. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02511940000106-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 September 2025. Download (5MB) | Request a copy

Abstract

Inhibitor adalah suatu zat yang diberikan pada lingkungan korosif untuk mengurangi laju korosi. Inhibitor korosi dari senyawa organik alami yang bersumber dari rempah-rempah, herbal aromatik, dan tanaman obat diteliti untuk untuk menggantikan inhibitor anorganik yang berbahaya, mahal, dan tidak ramah lingkungan. Penelitian pada ekstrak bunga cengkeh (Syzygium Aromaticum) dilakukan untuk mengetahui efektivitasnya sebagai Organic Green Corrosion Inhibitors (OGCIs) terhadap Baja API 5L Grade B pada lingkungan asam dan netral. Larutan elektrolit yang digunakan adalah NaCl 3,5% untuk lingkungan netral. Kemudian, asam asetat ditambahkan pada larutan tersebut untuk menciptakan lingkungan asam dengan pH 4. Untuk menghitung laju korosi, digunakan metode kehilangan berat (weight loss) dan polarisasi potensiodinamik. Kemudian dilakukan pengujian OES, GC-MS, EIS, XRD, dan FTIR untuk mendapatkan data pendukung dan menguatkan teori yang sudah ada. Variasi yang digunakan pada penelitian ini adalah konsentrasi inhibitor yang diberikan pada lingkungan korosif dan pH larutan. Hasil penelitian menunjukkan bahwa ekstrak bunga cengkeh dapat menjadi inhibitor korosi yang baik untuk Baja API 5L Grade B pada lingkungan asam dan netral, hal ini terjadi karena komponen utama pada ekstrak yaitu eugenol, eugenol acetate, dan caryophyllne dapat bereaksi pada permukaan baja dengan cara adsorpsi. Inhibitor ekstrak bunga cengkeh bekerja lebih efektif pada lingkungan asam dengan efisiensi mencapai 98,46% daripada lingkungan netral yang memiliki efisiensi 68,54%. Studi adsorpsi menunjukkan bahwa proses yang terjadi mengikuti Langmuir Adsorption Isotherm dengan proses adsorpsi melibatkan physical adsorption. Proses ini terjadi karena adanya gaya Tarik menarik van der waals antara senyawa inhibitor dengan permukaan logam.
====================================================================================================================================
Inhibitor is a substance given in a corrosive environment to reduce the rate of corrosion. Corrosion inhibitors from natural organic compounds sourced from spices, aromatic herbs and medicinal plants are being studied to replace inorganic inhibitors which are harmful, expensive and not environmentally friendly. Research was conducted on clove flower extract (Syzygium Aromaticum) to determine its effectiveness as Organic Green Corrosion Inhibitors (OGCIs) against API 5L Grade B Steel in acidic and neutral environments. The electrolyte solution used is 3,5% NaCl for a neutral environment. Then, acetic acid was added to the solution to create an acidic environment with a pH of 4. To calculate the rate of corrosion, weight loss and potentiodynamic polarization methods were used. Then OES, GC-MS, EIS, XRD, and FTIR tests were carried out to obtain supporting data and strengthen existing theory. Variations used in this study are the concentration of inhibitors given in a corrosive environment and the pH of the solution. The results showed that clove flower extract can be a good corrosion inhibitor for API 5L Grade B steel in acidic and neutral environments. Clove flower extract inhibitors work more effectively in an acidic environment with an efficiency reaching 98,46% than a neutral environment which has an efficiency of 68,54%. Adsorption studies show that the process that occurs follows the Langmuir Adsorption Isotherm with the adsorption process involving physical adsorption. This process occurs because of the van der Waals attraction between the inhibitor compound and the metal surface.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Ekstrak Bunga Cengkeh, Green Inhibitor, Korosi, Clove Flower Extract, Corrosion.
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA418.74 Corrosion and anti-corrosives T Technology > TA Engineering (General). Civil engineering (General) > TA462 Metal Corrosion and protection against corrosion T Technology > TA Engineering (General). Civil engineering (General) > TA467 Iron and Steel Corrosion and protection against corrosion
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Suli Rahayu Salsadillah
Date Deposited:	24 Jul 2023 13:53
Last Modified:	24 Jul 2023 13:53
URI:	http://repository.its.ac.id/id/eprint/99125

Actions (login required)

View Item