Pengaruh Nanopartikel Konduktif Fe3O4 Terhadap Nilai Tegangan Tembus Dari Kertas Yang Diresapi Nanofluid

Hutabarat, Ariel Kevin Samuel Hamonangan (2023) Pengaruh Nanopartikel Konduktif Fe3O4 Terhadap Nilai Tegangan Tembus Dari Kertas Yang Diresapi Nanofluid. Other thesis, Insitut Teknologi Sepuluh Nopember.

Text 07111940000101-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2025. Download (9MB)

Abstract

Pada penelitian ini dilakukan perendaman kertas isolasi press pada minyak mineral yang sudah dicampurkan nanopartikel Fe3O4 (nanofluida). Konsentrasi dari nanopartikel Fe3O4 yang digunakan berbeda-beda untuk melihat pengaruh dari penambahan nanopartikel Fe3O4 terhadap nilai tegangan tembus kertas isolasi press. Pada penelitian ini digunakan konsentrasi nanopartikel Fe3O4 0 g/L, 0,05 g/L, 0,1 g/L, 0,2 g/L, 0,3 g/L dan 0,4 g/L. Perendaman kertas isolasi press dilakukan selama 24 jam di dalam oven vakum dengan suhu 80 °C. Setelah selesai melakukan perendaman, dilakukan uji tegangan tembus pada kertas isolasi press. Pengujian tegangan tembus dilakukan menggunakan tegangan AC, dengan peningkatan tegangan yang bertahap sampai mencapai kegagalan. Hasil pengujian tegangan tembus menunjukkan kertas isolasi press yang direndam pada konsentrasi 0 g/L atau minyak mineral rata-rata mengalami kegagalan (tegangan tembus) pada tegangan 11,089 kV. Dengan penambahan konsentrasi Fe3O4 maka nilai tegangan tembus dari kertas isolasi press meningkat, konsentrasi Fe3O4 0,2 g/L menunjukan peningkatan nilai tegangan tembus tertinggi dengan nilai tegangan tembus 12,478 kV, setelah itu nilai tegangan tembus dari kertas isolasi menurun. Kertas isolasi press juga dilakukan pengujian SEM dan EDS, pengujian SEM menampilkan morfologi kertas isolasi press, sedangkan pengujian EDS menunjukan unsur yang terkandung pada kertas isolasi press. Melalui pengujian SEM dan EDS, dapat disimpulkan, semakin banyak nanopartikel Fe3O4 yang digunakan untuk perendaman kertas isolasi press, maka jumlah nanopartikel Fe3O4 yang dapat terdapat pada kertas isolasi press semakin banyak.

====================================================================================================================================

In this study, press insulation paper is impregnated in mineral oil mixed with Fe3O4 nanoparticles (nanofluid). The concentration of the Fe3O4 nanoparticles used is different to see the effect of the addition of Fe3O4 nanoparticles on the breakdown voltage of the press insulation paper. In this study, concentrations of Fe3O4 nanoparticles used are 0 g/L, 0.05 g/L, 0.1 g/L, 0.2 g/L, 0.3 g/L and 0.4 g/L. The insulation paper is impregnated for 24 hours in a vacuum oven at a temperature of 80 °C. After completing the impregnation, a breakdown voltage test is carried out on the insulating paper press. The breakdown voltage test is carried out using AC voltage, with a gradual increase in voltage until it reaches failure. The results of the breakdown voltage test showed that the insulation press impregnated at a concentration of 0 g/L or mineral oil failed on average (breakdown voltage) at a voltage of 11.089 kV. With the addition of the concentration of Fe3O4, the value of the breakdown voltage of the insulating paper press increased, the concentration of Fe3O4 0.2 g/L showed the highest increase in the value of the breakdown voltage with a breakdown voltage of 12.478 kV, after that the breakdown voltage value of the insulation paper decreased. Insulation press paper was also tested for SEM and EDS, SEM testing showed the morphology of press isolation paper, while EDS testing showed the elements contained in press isolation paper. Through SEM and EDS testing, it can be concluded that the more Fe3O4 nanoparticles used for immersing the insulating paper press, the more Fe3O4 nanoparticles that can be contained on the insulating paper press.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Fe3O4, Oil Insulation, Paper Insulation, Impregnation, Breakdown Voltage, Fe3O4, Kertas Isolasi, Minyak Isolasi, Perendaman, Tegangan Tembus.
Subjects:	T Technology > TK Electrical engineering. Electronics Nuclear engineering > TK3401 Insulation and insulating materials
Divisions:	Faculty of Intelligent Electrical and Informatics Technology (ELECTICS) > Electrical Engineering > 20201-(S1) Undergraduate Thesis
Depositing User:	Ariel Kevin Samuel Hamonangan Hutabarat
Date Deposited:	02 Aug 2023 07:04
Last Modified:	02 Aug 2023 07:04
URI:	http://repository.its.ac.id/id/eprint/99504

Actions (login required)

View Item