Pengaruh Mg Sebagai Dopan Pada Celah Energi Semikonduktor TiO2 Melalui Studi Eksperimen dan Komputasi

Oktavia, Linda Wati (2018) Pengaruh Mg Sebagai Dopan Pada Celah Energi Semikonduktor TiO2 Melalui Studi Eksperimen dan Komputasi. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 01211440000105-Undergraduate_Theses.pdf]
Preview
Text
01211440000105-Undergraduate_Theses.pdf - Accepted Version

Download (1MB) | Preview

Abstract

Pada penelitian ini dilakukan studi eksperimen dan komputasi untuk mengetahui pengaruh Mg terhadap celah energi TiO2. Pada studi eksperimen, senyawa TiO2 dan TiO2-Mg disintesis menggunakan metode hidrotermal. Selanjutnya, hasil sintesis dikarakterisasi dengan XRD, SEM, dan UV-DRS. Hasil dari eksperimen diperoleh nilai celah energi secara berturut yaitu TiO2 sebesar 3,1 eV, TiO2-Mg 0,5 mol% sebesar 2,9 eV, TiO2-Mg 1 mol% sebesar 2,6 eV dan TiO2-Mg 1,5 mol% sebesar 2,2 eV. Selain itu, pada studi komputasi dilakukan perhitungan sifat elektronik dari senyawa TiO2 dan TiO2-Mg. Hasil dari perhitungan tersebut diperoleh nilai energi pada pita konduksi dan pita valensi. Nilai pita valensi untuk TiO2 adalah sebesar -8,39 eV dan untuk pita konduksi sebesar -3,88 eV. Sedangkan tingkat energi dari Mg adalah sebesar -5,29 eV. Adanya tingkat energi dari Mg membuat driving force injeksi elektron dari LUMO pewarna ke pita konduksi semakin meningkat pada TiO2-Mg.
==============================================================================================================
In this research, the experimental and computational studies have been done to find out the effect of Mg addition into the band gap of TiO2. The experimental study, TiO2 and TiO2-Mg compounds were synthesized using hydrothermal methods. Furthermore, the synthesis results are characterized by XRD, SEM, and UV-DRS. The experimental results obtained that the band gap value of TiO2 is 3.1 eV and TiO2-Mg 1.5 mol% is 2.2 eV. While the computational study conducted calculations of electronic properties of the compounds TiO2 and TiO2-Mg. The calculation results obtained energy value in the conduction band and valence band. The valence band for TiO2 is -8.39 eV and for the conduction band is -3.88 eV. The energi level of Mg is -5.29 eV. The addition of Mg makes the TiO2-Mg conduction band lower than TiO2. The existane of Mg energy level makes the driving force for electrons injection from the LUMO dye is increase in the case of TiO2-Mg.

Item Type: Thesis (Undergraduate)
Additional Information: RSKi 621.312 44 Okt p-1 3100018074470
Uncontrolled Keywords: TiO2; TiO2-Mg; celah energi; doping; komputasi; band gap; doping; computation
Subjects: Q Science > QD Chemistry
T Technology > TJ Mechanical engineering and machinery > TJ810.5 Solar energy
Divisions: Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User: Linda Wati Oktavia
Date Deposited: 06 Apr 2018 06:26
Last Modified: 15 Sep 2020 05:39
URI: http://repository.its.ac.id/id/eprint/50391

Actions (login required)

View Item View Item