Studi Mix Design Beton Ringan Menggunakan Bahan Baku Limbah Karbon dan Pasir Silika untuk Mencapai Komposisi Optimal

Soeyandono, Jimmy Restu (2018) Studi Mix Design Beton Ringan Menggunakan Bahan Baku Limbah Karbon dan Pasir Silika untuk Mencapai Komposisi Optimal. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 10111310000021_Undergraduate_Theses.pdf]
Preview
Text
10111310000021_Undergraduate_Theses.pdf - Accepted Version

Download (3MB) | Preview

Abstract

Pada penelitian tugas akhir ini di mana melanjutkan penelitian tentang Pemanfaatan Beton Porus pada Panel Dinding Non Finishing. Dengan berfokus menentukan komposisi dari mix design beton ringan yang optimal untuk mendapatkan kekuatan, agar bisa digunakan sebagai pengisi dari dinding panel (non finishing wall). Komposisi desain campuran menggunakan pasir silika, limbah karbon untuk mencari komposisi yang paling optimal. Menggunakan tiga macam mix design densitas basah 700-800 kg/m3, rasio air semen 0,5 menggunakan pasir silika dan untuk limbah karbon dengan densitas basah 700-800 kg/m3 rasio air semennya 0,5. Mix design kedua dengan penambahan fly ash sebagai pengganti pasir dan limbah karbon sebesar 50 % dan mix design ketiga menggunakan pasir silika dengan perubahan komposisi semen dan fly ash sebesar 60 % Benda uji yang digunakan pada penelitian ini adalah silinder 15 cm, kubus 15 cm, SNI 03-1974-1990 untuk pengujian kuat tekan, SNI 03-0349-1989 untuk pengujian absorbsi, dan SNI 0096:2007 untuk pengujian Ketahanan Terhadap Rembesan. Hasil penelitian menunjukkan agregat yang menghasilkan kuat tekan terbaik adalah pasir silika dengan komposisi fly ash sebesar 60%. Dengan hasil kuat uji tekan sebesar 21,26 kg/cm2 untuk silinder dikonversi ke kubus sebesar 25,62 Kg/cm2 dan 24,33 kg/cm2 untuk benda uji kubus. Pengujian ketahanan terhadap rembesan air didapatkan benda uji tahan akan rembesan air. Dari penelitian ini dapat disimpulkan mix desain beton ringan dengan perbandingan 1 pasir : 1 semen, densitas basah 700 - 800 kg/m3, rasio air semen 0.5 dan menggunakan pasir Silika. SNI 03-0349-1989 menyebutkan bahwa syarat minimum kuat tekan rata-rata bata beton pejal mutu I sebesar 90 kg/cm2, mutu II sebesar 65 kg/cm2, mutu III sebesar 35 kg/cm2, dan mutu IV sebesar 25 kg/cm2 dan hasil mix design sudah memenuhi mutu IV.
==================================================================================================================
In this final project research where to proceed research about Utilization Concrete Porus on the Wall Panel Non Finishing . With focus determine composition from mix design lightweight concrete optimal for get strength, that bi sa used as filler from wall panel ( non finishing wall). Composition design mix use sand silica , waste carbon to search the most optimal composition . Use three kind of mix design density wet 700-800 kg / m 3, water-cement ratio of 0.5 using sand silica and for waste carbon with density wet 700-800 kg /m3 water ratio of cement 0.5. Mix the second design with addition fly ash as replacement sand and waste carbon amount 50 % and third mix design use sand silica with change cement composition and fly ash amount 60 % The test specimens used in this study were cylinders 15 cm, cubes 15 cm, SNI 03-1974-1990 for compressive strength test, SNI 03-0349-1989 for absorption test, and SNI 0096: 2007 for the testing of Resilience Against Seepage. The results showed that the aggregate that produces the best compressive strength is silica sand with composition fly ash by 60% . With results strong test press of 21 , 26 kg /cm2 for cylinder converted to cube of 25.62 Kg /cm2 and 24.33 kg/ cm2 for object test cube . Water resistance testing of water seepage obtained object resistant test will seepage of water. From this research can be concluded mix design of lightweight concrete with ratio 1 sand: 1 cement, density Wet 700-800 kg/ m3, water-cement ratio of 0.5 and using silica sand. SNI 03-0349-1989 states that the minimum requirement of compressive strength of average peak quality concrete brick is 90 kg / cm2 , the quality of II is 65 kg / cm2 , the quality of III is 35 kg / cm2 , and the quality of IV is 25 kg / cm2 and results mix design already meet quality IV

Item Type: Thesis (Undergraduate)
Additional Information: RSIS 620.136 23 Soe s-1 3100018074610
Uncontrolled Keywords: mix design; beton ringan; pasir silika; limbah karbon; mix design; lightweightconcrete; silica sand; carbon waste
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials.
T Technology > TP Chemical technology > TP884.L5 Lightweight concrete
Divisions: Faculty of Civil Engineering and Planning > Civil Engineering > 22301-(D4) Diploma 4
Depositing User: Soeyandono Jimmy Restu
Date Deposited: 23 Mar 2018 04:59
Last Modified: 07 Sep 2020 02:36
URI: http://repository.its.ac.id/id/eprint/50433

Actions (login required)

View Item View Item