Pengaruh Variasi pH Dan Temperatur Sintering Terhadap Nilai Sensitivitas Material TiO2 Sebagai Sensor Gas CO

Widianti, Ika Silviana (2015) Pengaruh Variasi pH Dan Temperatur Sintering Terhadap Nilai Sensitivitas Material TiO2 Sebagai Sensor Gas CO. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2711100065-Undergraduate_Theses.pdf - Published Version

Download (2MB) | Preview
[img]
Preview
Text
2711100065-Presentation.pdf - Presentation

Download (2MB) | Preview
[img]
Preview
Text
2711100065-Paper.pdf - Published Version

Download (691kB) | Preview

Abstract

Telah dilakukan berbagai macam pengupayaan untuk mengoptimalkan potensi Titanium dioksida (TiO2) sebagai sensor gas, mengingat TiO2 merupakan semikonduktor metal oksida. Pada penelitian ini digunakan TiO2 dalam bentuk serbuk, dengan pelarutnya H2SO4 yang diencerkan dengan air distilasi sehingga terbentuk variasi pH 1, 3, dan 5. Metode sol-gel dilakukan dengan perendaman dan dilanjutkan stiring selama 2,5 jam, kecepatan 700 rpm, dan temperatur 200ºC . Drying dilakukan selama 2 jam pada temperatur C, selanjutnya serbuk dikompaksi pada tekanan 200 bar agar terbentuk pellet. Pelet kemudian disintering pada temperatur 700ºC, 800ºC, dan 900ºC selama 1 jam. Karakterisasi material dilakukan dengan Scanning Electron Microscope (SEM) dan X-Ray Diffraction (XRD). Sedangkan untuk luas permukaan spesifik sampel TiO2 diuji dengan BET Analyser. Morfologi TiO2 yang dihasilkan dari proses sol-gel berbentuk bulat (spherical) dan memiliki ukuran kristal 69,74 nm. Nilai sensitivitas didapatkan dari pengujian sensitivitas pada temperatur 100ºC dan variasi volume gas CO 5L, 12,5L, 25L. Respon terbaik adalah material TiO2 pH 3 yang disinter dengan temperatur 900ºC, serta memiliki ukuran pori 50,83 nm. ========== It has been done various efforts to optimize titanium dioxide (TiO2) potential as a gas sensor material, since TiO2 is a semiconductor metal oxide. In this research TiO2 powder is used with H2SO4 as the solvent dissolved in distilled water to make various pH such as 1,3, and 5. The sol-gel method is done through submersion and samples is stirred 2,5 hours with 700 rpm speed, and 200ºC until the gel formed. Drying process is done by 2 hours holding at 350ºC, then the powder is compacted with 200 bar pressure to make pellets. Pellets are sintered at 700, 800, 900ºC for 1 hour. Material characterization is done by using Scanning Electron Microscope (SEM) and X-Ray Diffraction (XRD). Meanwhile, to identify spesific surface area of the TiO2 sample is tested using BET Analyser. The morphology of TiO2 by using sol-gel method are spherical in shape and have 69,74 nm crystal size. Sensitivity values are got from sensitivity test on 100ºC and variation of CO gas volume 5L, 12,5L, and 25L. The best response is found on material TiO2 pH 3 which is sintered at 900ºC, and also has porous size of 50,83 nm .

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 681.25 Wid p
Uncontrolled Keywords: titanium dioksida (TiO2), pH, metode sol-gel, sintering, nilai sensitivitas, gas CO, titanium dioxide (TiO2), pH, sol-gel method, sinter, sensitivity value, CO gas
Subjects: T Technology > TK Electrical engineering. Electronics Nuclear engineering > TK7871.674 Detectors. Sensors
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: - Davi Wah
Date Deposited: 21 Mar 2019 09:01
Last Modified: 21 Mar 2019 09:01
URI: https://repository.its.ac.id/id/eprint/62565