Pengaruh Variasi Konsentrasi Metanol Terhadap Sifat Permeabilitas Metanol Dari Membran Komposit Kitosan/monmorillonit Termodifikasi Silan 10%

Wulansari, Diah Ayu (2016) Pengaruh Variasi Konsentrasi Metanol Terhadap Sifat Permeabilitas Metanol Dari Membran Komposit Kitosan/monmorillonit Termodifikasi Silan 10%. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 1412100049-undergraduate theses.pdf]
Preview
Text
1412100049-undergraduate theses.pdf - Accepted Version

Download (1MB) | Preview
[thumbnail of 1412100049-paperpdf.pdf]
Preview
Text
1412100049-paperpdf.pdf - Accepted Version

Download (545kB) | Preview
[thumbnail of 1412100049-presentationpdf.pdf]
Preview
Text
1412100049-presentationpdf.pdf - Presentation

Download (2MB) | Preview

Abstract

Membran komposit yang terdiri dari kitosan sebagai
matriks dan monmorillonit sebagai filler telah berhasil dibuat.
Kitosan yang digunakan dalam pembuatan membran memiliki
derajat deasetilasi (DD) sebesar 70,225 %. Monmorillonit yang
digunakan telah dimodifikasi dengan silan 10 %. Membran
komposit tersebut dibuat untuk mengetahui sifat permeabilitas
metanol pada lima variasi konsentrasi metanol yang digunakan.
Konsentrasi metanol yang digunakan dalam penelitian ini
adalah 1, 2, 3, 4 dan 5 M. Sifat–sifat membran yang
dikarakterisasi yaitu gugus fungsi dengan menggunakan FTIR
(Fourier Transform Infra Red), water uptake dan methanol
uptake, sedangkan uji kinerja membran dilakukan dengan
pengukuran permeabilitas metanol dengan menggunakan alat
uji permeabilitas. Nilai permeabilitas yang diperoleh semakin
menurun seiring dengan meningkatnya konsentrasi metanol
yang digunakan. Permeabilitas metanol tertinggi yang
diperoleh sebesar 4,7771 x 10-5 cm2/s pada konsentrasi 1 M dan
2 M, sedangkan nilai permeablitas metanol terendah sebesar
1,9108 x 10-5 cm2/s pada konsentrasi metanol 5 M. ========== Composite membrane composing of chitosan as a
matrix and monmorillonit as filler has been conducted
succesfully. Chitosan was used in the making of the membrane
has a degree of deacetylation (DD) of 70.225%. Prior to be used
monmorillonit has been modified with silane 10%. The
composite membrane was made to determine the methanol
permeability using five variations methanol concentration. The
concentration of the methanol used in this research were 1, 2,
3, 4, and 5 M. The properties of the membrane were
characterized by FTIR (Fourier Transform Infra Red), water
uptake, and methanol uptake, whereas the performance of
membrane conducted by measuring methanol permeability.
Obtaining permeability decreases along with increase the
concentration of methanol used. The highest methanol
permeability is 4.7771 x 10-5 cm2/s both at concentration of 1
and 2 M, while the lowest methanol permeability is 1.9108 x
10-5 cm2/s at concentration of 5 M.

Item Type: Thesis (Undergraduate)
Additional Information: RSKi 573.774 Wul p 3100017068931
Uncontrolled Keywords: Kitosan, Monmorillonit, Silan, Membran, dan Permeabilitas Metanol, Chitosan, Monmorillonite, Silane, Membrane, and Methanol Permeability
Subjects: Q Science > QH Biology > QH601 Cell membranes
Divisions: Faculty of Mathematics and Science > Biology > 46201-(S1) Undergraduate Thesis
Depositing User: - Davi Wah
Date Deposited: 13 Nov 2019 03:02
Last Modified: 13 Nov 2019 03:02
URI: http://repository.its.ac.id/id/eprint/71709

Actions (login required)

View Item View Item