Karakterisasi Arus Dan Tegangan (I-V) Pada Dye Sensitized Solar Cell (Dssc) Dengan Tio2 Terdoping Nitrogen Menggunakan Dye Sensitizer N749

Gunawan, Bodi (2016) Karakterisasi Arus Dan Tegangan (I-V) Pada Dye Sensitized Solar Cell (Dssc) Dengan Tio2 Terdoping Nitrogen Menggunakan Dye Sensitizer N749. Masters thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
1114201011-master-theses-.pdf - Published Version

Download (2MB) | Preview

Abstract

Nanokristal TiO2 terdoping nitrogen sebagai bahan dasar fotoanoda dyesensitized solar cell (DSSC) telah berhasil dianalisis dan dikarakterisasi. TiO2 terdoping nitrogen fase anatase disintesis dengan menggunakan metode kopresipitasi. TiCl3 sebagai bahan perkusor dicampur dengan amonia sebagai sumber dopan nitrogen dengan beberapa variasi konsentrasi amonia yaitu 2, 5, dan 7,5%. Kemudian endapan yang dihasilkan disaring lalu dikeringkan dan dikalsinasi dengan suhu 400ºC selama 3 jam. Uji XRD dan UV-Vis dilakukan untuk mengetahui ukuran kristal, spektal absorbansi dan band-gap pada masingmasing sampel. Analisis XRD menunjukkan ukuran kristal TiO2 terdoping nitrogen berkisar antara 7,4 – 9,9 nm sedangkan band-gap untuk sampel dengan penambahan amonia 2, 5, dan 7,5% masing-masing adalah 3,0; 2,7 dan 2,5 eV. Hasil karakterisasi I-V dilakukan pada modul-modul sel surya dengan fotoanoda TiO2 terdoping nitrogen menunjukkan performa terbaik terdapat pada modul DSSC dengan penambahan amonia 7,5% dengan nilai rapat arus 0,784 mA/cm-2 dan efisiensi 0,18% =========================================================== cell has been successfully characterized and analyzed. The anatase phase of N-doped TiO2 synthesized by co-precipitation method. TiCl3 as a precursor mixed with ammonia solution with various concentrations, namely, 2, 5 and 7.5%, and calcinated at temperature 400ºC over 3 hours. X-ray diffraction (XRD) and UVVis spectroscopy were performed to analyze a crystal size and band gap of the samples. The XRD data showed that the crystal size of N-doped TiO2 was 7.4 - 9.9 nm and the measured band gap around 2.64 eV, respectively. I-V characterization of solar cell module shown that the highest power conversion efficiency was the solar cell module that fabricated with 7.5% of ammonia solution with the short circuit current (Jsc) and the efficiency was at 0.784 mA/cm-2 and 0.18%, respectively.

Item Type: Thesis (Masters)
Additional Information: RTFi 621.312 44 Gun k
Uncontrolled Keywords: band-gap, DSSC, efisiensi, TiO2 terdoping nitrogen
Subjects: Q Science > QC Physics > QC475 Photoluminescence
Divisions: Faculty of Mathematics and Science > Physics > 45101-(S2) Master Thesis
Depositing User: EKO BUDI RAHARJO
Date Deposited: 02 Dec 2019 11:32
Last Modified: 02 Dec 2019 11:32
URI: https://repository.its.ac.id/id/eprint/72166

Actions (login required)

View Item View Item