Pengaruh Waktu Celup Terhadap Sifat Adhesive, Ketebalan Lapisan Dan Ketahanan Korosi Pada Baja API 5L Dengan Hot DIP Galfan (Zn-5% Al)

., Ibrahim (2016) Pengaruh Waktu Celup Terhadap Sifat Adhesive, Ketebalan Lapisan Dan Ketahanan Korosi Pada Baja API 5L Dengan Hot DIP Galfan (Zn-5% Al). Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2712100102-Undergraduate_Thesis.pdf - Accepted Version

Download (3MB) | Preview
[img]
Preview
Text
2712100102-Paper.pdf - Accepted Version

Download (698kB) | Preview
[img]
Preview
Text
2712100102-Presentation.pdf - Presentation

Download (1MB) | Preview

Abstract

Baja menjadi sangat mudah terkorosi ketika berada dalam lingkungan yang korosif. Coating merupakan salah satu metode proteksi korosi untuk baja. Coating menggunakan metode hot dip galfan dapat dijadikan solusi untuk proteksi korosi pada baja. Kualitas hasil coating ditentukan oleh beberapa factor diantaranya adalah sifat adhesive, ketebalan dan ketahanan korosi, dimana ketiganya dipengaruhi oleh waktu pencelupan. Penelitian ini menganalisis pengaruh waktu celup terhadap sifat adhesive, ketebalan, dan ketahanan korosi lapisan. Waktu celup yang digunakan adalah 1,5,9, dan 13 meni pada temperatur 450oC. Pada penelitian ini telah dilakukan pengujian SEM, Metallography, XRD, Thickness Test, Adhesive Test, dan Weight loss. Berdasarkan hasil pengujian, nilai ketebalan maksimum adalah 288.9µm, nilai kekuatan adhesive maksimum adalah 8,05 Mpa, dan nilai ketahanan korosi yang paling optimum adalah 0.0229mmpy. Nilai ketebalan dan sifat adhesive yang dihasilkan dipengaruhi oleh itermetallic layer yang terbentuk. Waktu pencelupan 1 menit memiliki struktur mikro intermetallic layer yang berbeda dibandingkan dengan variable waktu celup yang lainnya. Senyawa intermetallic yang terbentuk adalah Fe2Al5. ================================================================================================== Steel is easily corroded in a corrosive environtment. Coating is a method of corrosion protection for a steel. Hot dip galfan coating is able to be a solution for corrosion protection for a steel. The quality coating is determined by several factors, there are adhesive properties, thickness, and corrosion resistance of coating, all of whom are affected by immersion time. This research analyzed the effect of immersion time to the adhesive properties , thickness , and corrosion resistance of coating. The immersion time that used are 1,5,9 , and 13 minutes at 450oC . This research has been evaluated by several test, there are SEM , Metallography , XRD , Thickness Test , Adhesive Test , and Weight loss. Based on the test results , the maximum thickness value is 288.9μm , maximum adhesive strength value is 8.05 Mpa , the most excellent corrosion resistance value is 0.0229 mmpy. The value of the thickness and properties of the resulting adhesive layer is affected by itermetallic formed . The immersion time of 1 minute has the microstructure intermetallic layer that is different than the other variable immersion time . Intermetallic compounds formed is Fe2Al5 .

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 671.732 Ibr p 3100016067561
Uncontrolled Keywords: Hot dip Zn-5%Al, Immersion time, Adhesive strength, Corrosion resistance, waktu celup, Ketebalan, Sifat Adhesive, Ketahanan korosi
Subjects: T Technology > TS Manufactures > TS670 Electroplating
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: - Davi Wah
Date Deposited: 25 Feb 2020 07:37
Last Modified: 25 Feb 2020 07:37
URI: https://repository.its.ac.id/id/eprint/75109