Sintesis Zeolit Y Dari Kaolin Bangka Belitung Secara Langsung Dengan Variasi Waktu Kristalisasi

Junaydi, Ahmad (2016) Sintesis Zeolit Y Dari Kaolin Bangka Belitung Secara Langsung Dengan Variasi Waktu Kristalisasi. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
1412100039-Undergraduate_Thesis.pdf - Accepted Version

Download (2MB) | Preview

Abstract

Penelitian ini bertujuan untuk mengetahui pengaruh waktu kristalisasi terhadap sintesis zeolit Y dari kaolin secara langsung (tanpa metakaolinisasi). Zeolit Y disintesis melalui tiga tahap, yaitu pembuatan seed gel, pembuatan feedstock gel dan pembuatan overall gel yang diikuti dengan proses hidrotermal. Padatan hasil sintesis dikarakterisasi menggunakan spektroskopi infra merah (FTIR), difraksi sinar-X (XRD), Scanning Electron Microscopy–Energy Dispersive X-ray (SEM-EDX). Hasil karakterisasi XRD dan FTIR menunjukkan bahwa fase zeolit Y terbentuk pada waktu kristalisasi 4-12 jam dengan intensitas yang semakin meningkat dan mengalami penurunan pada waktu 18-24 jam. Fase pengotor zeolit P terbentuk pada waktu kristalisasi 4-12 jam, setelah itu mengalami penurunan pada waktu 18-24 jam. Fase pengotor lain hidroksi sodalit terbentuk dengan intensitas yang meningkat pada waktu 4-24 jam. Waktu kristalisasi tidak begitu berpengaruh terhadap perbedaan ukuran agregat partikel dan rasio SiO2/Al2O3 produk yang dihasilkan. ================================================================================================================== The purpose of this research was to study the effect of crystallization time on the direct synthesis of zeolite Y from kaolin (without metakaolination). Zeolite Y was synthesized through three stages, namely compounding seed gel, compounding feedstock gel and making overall gel followed by hydrothermal process. Solid products obtained were characterized using infrared spectroscopy (FTIR), X-ray diffraction (XRD), Scanning Electron Microscopy-Energy Dispersive X-ray (SEMEDX). The result of XRD and FTIR characterization indicate that the zeolite Y phase formed with increasing of intensity at crystallization time 4-12 hours and decreased at 18-24 hours. Impurity phase zeolite P formed at crystallization time 4-12 hours, after that it decreased at 18-24 hours. Another impurity phases hydroxy sodalite formed with increasing intensity at 4-24 hours. Crystallization time difference was not so influential on aggregate particle size and ratio of SiO2/Al2O3 of products.

Item Type: Thesis (Undergraduate)
Additional Information: RSKi 549.68 Jun s
Uncontrolled Keywords: Hidroksi sodalit, Kaolin, Zaolit P., Zeolit Y, waktu kristalisasi, Crystallization time, Hydroxy sodalite, Zeolite P. Zeolite Y
Subjects: T Technology > TP Chemical technology > TP159.M6 Zeolites
Divisions: Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User: ansi aflacha
Date Deposited: 28 Jul 2020 03:23
Last Modified: 28 Jul 2020 03:23
URI: https://repository.its.ac.id/id/eprint/76582

Actions (login required)

View Item View Item