Analisis Tegangan Proyektil Frangible Pada Proses Ejeksi Dengan Variasi Koefisien Gesek Dan Penambahan Split Cetakan Menggunakan Metode Elemen Hingga

Jati, Muhammad Mulya (2020) Analisis Tegangan Proyektil Frangible Pada Proses Ejeksi Dengan Variasi Koefisien Gesek Dan Penambahan Split Cetakan Menggunakan Metode Elemen Hingga. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02511640000112-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (3MB) | Request a copy

Abstract

Proses kompaksi merupakan salah satu langkah pembuatan proyektil frangible. Proses tersebut meliputi fase kompresi dan ejeksi yang dapat dipengaruhi oleh desain cetakan. Pada prakteknya, proyektil yang dihasilkan memiliki retak dan permukaan yang kasar. Tujuan penelitian ini adalah memahami pengaruh koefisien gesek dan penambahan split cetakan terhadap tegangan yang dialami proyektil frangible pada proses ejeksi. Simulasi dilakukan menggunakan metode ANSYS Workbench Mechanical Analysis Type Explicit Dynamic pada 3 desain cetakan dan variasi koefisien gesek. Hasil penelitian menunjukan desain yang memiliki split mengurangi tegangan yang terjadi selama proses ejeksi. Hasil penelitian juga menunjukan koefisien gesek memberikan dampak pada besaran gaya ejeksi. Semakin besar nilai koefisien gesek semakin besar gaya ejeksi yang diperlukan. Gaya ejeksi yang tinggi adalah indikasi kondisi tegangan sub-optimal proyektil pasca-pembebanan. Penelitian ini bermanfaat untuk menindaklanjuti tegangan yang dialami proyektil dan kekuatan ejeksi sebagai faktor yang efektif untuk mengidentifikasi dan mengurangi risiko cacat proyektil sehingga proyektil memiliki akurasi dan presisi yang baik.

====================================================================================================================

The compaction process is one of the steps for making frangible projectiles. The process includes compression and ejection phases which can be affected by the mold design. In practice, the resulting projectile have cracks and rough surfaces. The purpose of this study was to determine the effect of the friction coefficient and the addition of a split mold on the stress applied by the frangible projectile in the ejection process. The simulation was carried out with the ANSYS Workbench Mechanical Analysis Type Explicit Dynamic method on 3 mold designs and variations of the friction coefficient. The results showed that the split design reduces the stress that occurs during the ejection process. The results also show that the friction coefficient has an effect on the magnitude of the ejection force. The greater the friction coefficient, the greater the ejection force required. The high ejection force is an indication of the sub-optimal projectile stress conditions after loading. This research is useful for following up the pressure applied by projectiles and ejection strength as an effective factor to identify and reduce the risk of projectile defects so that projectiles have good accuracy and precision.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Desain Cetakan, Koefisien Gesek, Gaya Ejeksi, Proyektil, Frangible Design, Friction Coefficient, Ejection Force, Projectile, Frangible
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA347 Finite Element Method
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Muhammad Mulya Jati
Date Deposited:	13 Aug 2020 04:18
Last Modified:	26 May 2025 01:50
URI:	http://repository.its.ac.id/id/eprint/77982

Actions (login required)

View Item