Pengujian Pelet Hasil Mesin Ekstruder Tipe Single Screw Dari Material Campuran Biokomposit

Mulyono, Arfian Hendra (2020) Pengujian Pelet Hasil Mesin Ekstruder Tipe Single Screw Dari Material Campuran Biokomposit. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
02111240000138-Undergraduate_Theses.pdf
Restricted to Repository staff only

Download (3MB) | Request a copy

Abstract

Plastik kini telah menjadi barang yang hampir tidak bisa terpisahkan dalam kehidupan manusia, contohnya seperti botol plastik, helm, kantong plastik, dan bodykit motor maupun mobil. Banyak industri-industri di indonesia menggunakan bahan plastik sebagai material utama produknya. Pada tanggal 20 Oktober 2008 Badan Perserikatan Bangsa-Bangsa (PBB) melalui FAO pada pertemuan dunia di Roma, Italia, mencanangkan tahun 2009 sebagai International Year of Fibers. Hal tersebut terkait dengan pemanfaatan berbagai serat alam menjadi sumber bahan baku dalam berbagai produk industri. Dengan pemanfaatan tersebut diharapkan dapat menanggulangi dua hal yaitu sebagai solusi terhada p perubahan iklim dan dampaknya terhadap kelestarian lingkungan. Serat sisal (Agave Sisallana Perrine) dipilih karena memiliki kekuatan yang baik dan elastis sehingga berpotensi sebagai bahan komposit yang murah, ringan dan kuat serta mudah dibudidayakan. Dengan mengkaji beberapa eksperimen yang dilakukan sebelumnya, masih perlu dilakukan eksperimen berkaitan dengan komposit serat sisal mengingat bahwa masih banyaknya biodiversitas serat alam yang ada di Indonesia, sedangkan eksperimen sebelumnya menghasilkan pelet biokomposit serat sisal yang belum sempurna Data yang akan diambil dalam eksperimen adalah temperatur leleh serta prosentase void biokomposit sebagai properti yang penting dalam pemanfaatan serat sisal sebagai filler biokomposit. Atas dasar permasalahan diatas maka dilaksanakan studi eksperimental pengaruh komposisi pelet biokomposit terhadap sifat thermal dan struktur potongan melintang mengunakan mesin ekstruder tipe single screw. Metode yang digunakan pada penelitian tugas akhir ini adalah membuat campuran Polypropylene (PP), Maleic Anhydride Polypropylene (MAPP) dan Serat Sisal dengan komposisi sebagai berikut: Biokomposit A terdiri dari 90% material PP, 5% material serat sisal, dan 5% MAPP, biokomposit B terdiri dari 8 0% material PP, 15% serat sisal, 5% MAPP, biokomposit C terdiri dari 70% material PP, 25% serat sisal, 5% MAPP. Bahan biokomposit kemudian dicetak sehingga berbentuk pelet. Selanjutnya pelet diukur temperatur lelehnya dengan DSC (Differential Scanning Calorimetry). Kemudian dilanjutkan dengan pengamatan dengan mikroskop untuk melihat kualitas setiap pelet biokomposit berdasarkan prosentase voidnya di laboratorium Metallurgi Teknik Mesin ITS. Hasil yang diharapkan adalah mesin ekstruder yang digunakan dapat berfungsi dengan baik dan didapatkan hasil pelet yang selanjutnya akan dilakukan eksperimen pengaruh pelet yang sudah jadi terhadap sifat thermal dan struktur potongan melintang. Kata kunci: Polypropylene, Serat Sisal, Maleic Anhydride Polypropylene, Biokomposit . ========================================================= Plastic has now become an almost inseparable item in human life, for example, such as plastic bottles, helmets, plastic bags, and motorcycle and car body kits. Many industries in Indonesia use plastic as the main material for their products. On 20 October 2008 the United Nations (UN) through the FAO at the world meeting in Rome, Italy, declared the year 2009 as the International Year of Fibers. This is related to the use of various natural fibers as a source of raw materials for various industrial products. With this utilization, it is expected to be able to overcome two things, namely as a solution to climate change and its impact on environmental sustainability. Sisal fiber (Agave Sisallana Perrine) was chosen because it has good strength and elasticity so that it has the potential to be a composite material that is cheap, light and strong and easy to cultivate. By reviewing some of the previous experiments, it is still necessary to conduct experiments related to sisal fiber composites considering that there is still a large number of natural fiber biodiversity in Indonesia, while previous experiments have resulted in imperfect sisal fiber biocomposite pellets.The data to be taken in the experiment is the melting temperature and The percentage of biocomposite voids as an important property in the utilization of sisal fiber as a biocomposite filler. Based on the above problems, an experimental study was carried out on the effect of the composition of the biocomposite pellets on the thermal properties and the structure of the cross section using a single screw type extruder machine. The method used in this research is to make a mixture of Polypropylene (PP), Maleic Anhydride Polypropylene (MAPP) and Sisal Fiber with the following composition: Biocomposite A consists of 90% PP material, 5% sisal fiber material, and 5% MAPP. biocomposite B consists of 80% PP material, 15% sisal fiber, 5% MAPP, biocomposite C consists of 70% PP material, 25% sisal fiber, 5% MAPP. The biocomposite material is then printed to form pellets. Next are pellets, The melting temperature was measured by using DSC (Differential Scanning Calorimetry). Then proceed with microscopic observations to see the quality of each biocomposite pellet based on the percentage of voids in the Metallurgi Mechanical Engineering ITS laboratory. The expected result is that the extruder machine used can function properly and the results of the pellets will be obtained which will then be carried out experiments on the effect of the finished pellets on the thermal properties and structure of the cross section. Keywords: Polypropylene, Sisal Fiber, Maleic Anhydride Polypropylene, Biocomposite.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Polypropylene, Serat Sisal, Maleic Anhydride Polypropylene, Biokomposit .
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Faculty of Industrial Technology > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User: Arfian Hendra Mulyono
Date Deposited: 03 Sep 2020 06:02
Last Modified: 03 Sep 2020 06:02
URI: https://repository.its.ac.id/id/eprint/81748

Actions (login required)

View Item View Item