Pengaruh Variasi Komposisi Serbuk Kayu Dengan Pengikat Semen Pada Pasir Cetak Terhadap Cacat Porositas Dan Kekasaran Permukaan Hasil Pengecoran Aluminium Alloy 6061

Rohman, M. Fatkhur (2014) Pengaruh Variasi Komposisi Serbuk Kayu Dengan Pengikat Semen Pada Pasir Cetak Terhadap Cacat Porositas Dan Kekasaran Permukaan Hasil Pengecoran Aluminium Alloy 6061. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2111106010-Undergraduate-Thesis.pdf - Accepted Version

Download (1MB) | Preview

Abstract

Proses pengecoran dilakukan dengan cara mencairkan logam dalam dapur pelebur, kemudian dituangkan ke dalam cetakan dan dibiarkan membeku hingga dapat dikeluarkan dari dalam cetakan. Metode pengecoran yang paling sering digunakan adalah pengecoran cetakan pasir (sand casting). Faktor yang berpengaruh terhadap kualitas hasil pengecoran cetakan pasir, diantaranya adalah komposisi cetakan pasir dan perancangan sistem saluran (gatting system). Penentuan komposisi cetakan pasir dan perancangan sistem saluran harus tepat untuk mencegah cacat yang sering terjadi dan untuk mendapatkan hasil coran yang optimal. Salah satu komposisi utama cetakan pasir adalah pasir cetak, pasir silika, semen, dan air, dengan bahan penambah berupa serbuk kayu yang berfungsi untuk meningkatkan sifat colapsability dari sebuah cetakan. Pada penelitian ini bertujuan untuk menganalisa pengaruh variasi komposisi serbuk kayu dengan pengikat semen pada pasir cetak terhadap cacat porositas dan kekasaran permukaan hasil pengecoran aluminium alloy 6061. ================================================================================================================= Casting process is done by means of a metal melt in the fuser kitchen, then poured into molds and allowed to set up to be taken out of the mold. Casting method most commonly used is sand casting. Factors that affect the quality of sand casting, including the composition of the sand molds and designing gatting systems. Determination of the composition of the sand molds and designing the duct system must be appropriate to prevent defects that often occur and to obtain optimal results castings. One of the main composition is a sand mold molding sand, silica sand, cement, and water, with an addition of materials such as wood dust which serves to improve the properties of a mold colapsability. In this study aims to analyze the effect of variations in the composition of wood dust with cement binder in molding sand against defects porosity and surface roughness of an aluminum casting alloy 6061.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Sand Casting, Aluminium Alloy 6061, Porositas, Kekasaran Permukaan
Subjects: T Technology > TS Manufactures > TS233 Sand casting. Metal castings--Thermal properties.
Divisions: Faculty of Industrial Technology > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User: Yeni Anita Gonti
Date Deposited: 17 Dec 2020 06:33
Last Modified: 17 Dec 2020 06:33
URI: https://repository.its.ac.id/id/eprint/82313

Actions (login required)

View Item View Item