Pambudi, Muhammad Rizal (2017) Perancangan Sistem Proteksi Katodik Arus Paksa pada Pipa Baja API 5L Grade B di Dalam Tanah Dengan Variasi Jenis Coating. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
2713100004-Undergraduate_Theses.pdf - Published Version Download (1MB) | Preview |
Abstract
Impressed Current Cathodic Protection (ICCP) adalah suatu metode yang bertujuan untuk mencegah korosi pada material baja atau besi. Metode ini bekerja dengan membalikkan arah arus korosi atau listrik dalam proses korosi sehingga arus listrik searah mengalir keseluruh permukaan logam melalui elektrolit. Proteksi katodik arus paksa dipilih karena mudah untuk mengontrol arus yang diberikan dalam sistem. Pada ICCP, anoda yang digunakan adalah material inert sehingga mempunyai masa aktif yang lebih lama. Material seperti platinum, magnet, baja silikon, dan grafit biasanya digunakan pada pengaplikasian tersebut. Adapaun untuk katoda digunakan Pipa Baja. Tujuan dalam penelitian ini adalah untuk merancang proteksi katodik pada pipa dengan tipe API 5L dengan variabel coating. Variabel yang digunakan pada penelitian ini adalah perbedaan jenis pelapisan yaitu base coat dan top coat. Dimensi panjang pipa API 5L yang digunakan adalah 1,5m. Pengukuran yang dilakukan adalah pengukuran resistivitas tanah dan pH pada tanah tempat pipa digunakan. Pada katoda dengan penggunaan coating sekunder dan primer maka arus proteksi yang diperlukan akan semakin rendah dibandingkan dengan katoda yang hanya menggunakan coating primer. Sementara pada kondisi lingkungan dengan resistivitas tanah yang berbeda, semakin tinggi resistivitas tanah maka mengakibatkan kebutuhan arus proteksi semakin rendah. ======================================================================================================================== Impressed Current Cathodic Protection (ICCP) is a method that aims to prevent corrosion of steel or iron material. This method works by reversing the direction of corrosion or electric current in the corrosion process so that an electric current uniformly flows throughout the metal surface through the electrolyte. Cathodic protection of forced current is chosen because it is easy to control the current given in the system. In ICCP, the anode used is an inert material so it has a longer active period. Materials such as platinum, magnets, silicon steel, and graphite are commonly used in such applications. Adapaun for cathode used Steel Pipe. The purpose of this research is to design cathodic protection on pipe with API type 5L with coating variable. The variables used in this study are different types of coatings namely base coat and top coat. The 5L API pipe length dimension used is 1.5m. Measurements taken are the measurement of soil resistivity and pH on the ground where the pipe is used. At the cathode with the use of secondary and primary coatings the required protective current will be lower than that of the cathode using only the primary coating. While in environmental conditions with different soil resistivity, the higher the soil resistivity will result in lower protection requirement.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Uncontrolled Keywords: | Anoda, Katoda, Korosi, Proteksi Katodik Arus Paksa |
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) > TA418.74 Corrosion and anti-corrosives |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | Pambudi Muhammad Rizal |
| Date Deposited: | 07 Sep 2017 08:04 |
| Last Modified: | 05 Mar 2019 07:12 |
| URI: | http://repository.its.ac.id/id/eprint/43303 |
Actions (login required)
 |
View Item |