Abadi, Fany Rahmansah (2015) Pengaruh Kombinasi Ukuran Partikel Cu Dan Temperatur Sintering Terhadap Sifat Mekanik Dan Densitas Komposit W-Cu. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
2710100075-Paper.pdf - Published Version Download (1MB) | Preview |
Preview |
Text
2710100075-Undergraduate Theses.pdf - Published Version Download (7MB) | Preview |
Preview |
Text
2710100075-Presentation.pdf - Presentation Download (4MB) | Preview |
Abstract
Proyektil adalah bagian dari peluru yang dioptimalkan
agar proyektil mempunyai kemampuan untuk menembus yang
tinggi dan jangkaukan yang luas. Material yang biasa digunakan
dalam pembuatan peluru adalah timbal. Namun timbah
merupakan material beracun yang dapat membahayaakan tubuh.
Oleh karena itu pada penelitian ini digunakan material alternatif
dari komposit tungsten dan tembaga (WCu) sebagai material
alternatif dalam pembuatan proyektil peluru
Pembuatan dilakukan dengan proses metalurgi iserbuk
dengan berat Cu 20% dari berat total komposit. Variabel yang
digunakan adalahi ukuran partikel Cu 20-25, 30,35 dan 30-35μm
dan temperatur sintering 1100, 1200 dan 1300oC. Proses ini
dilakukan dengan tekanan kompaksi 600 Mpa dan waktu tahan
selama 3 jam. Setelah itu secara berturut-turunt dilakukan
pengujian densitas, kekerasan, SEM, XRD dan uji tekan.
Berdasarkan hasil pengujian, fasa yang terbentuk dari
hasil XRD adalah W dan Cu, sinter density tertinggi sebesar
12.78 g/cm3dan porositas terkecil sebesar 20,46% pada saat
ukuran partikel Cu 20-25 μm dengan temperatur sintering
1300oC. Kekuatan tekan tertinggi sebesar 261,82 Mpa pada 20-
25μm-1300oC, modulus elastisitas tertinggi sebesar 58,31 Gpa
pada 20-25μm 1300oC. ========== Projectile is part of the bullets that optimized to be the
bullet has a high range and penetrating. Usually, The material
used in the manufacture of bullets is Pb . However Pb a toxic
material that can dangerous for body. Therefore in this study
used an alternative material of the composite tungsten and
copper (WCU) as an material in the manufacture of a bullet
Manufacture of composite made by powder metallurgy
process with Cu 20% of the total weight of Composite. The
variables used were Cu particle size 20-25, 30.35 and 30-
35μm and temperature sintering 1100, 1200 and 1300oC. This
process is done by compacting pressure of 600 MPa and
holding time for 3 hours. After that, perform the testing
density, hardness, SEM, XRD and pressure tests of composite.
Based on test results, a phase which is formed from
the results of XRD is W and Cu, sinter highest density of 12.78
g / cm3 and the smallest porosity of 20.46% when the particle
size of 20-25 μm Cu sintering temperature 1300oC. The
highest compressive strength of 261.82 MPa at 20-25μm-
1300oC, the highest elasticity modulus of 58.31 GPa at 1300oC
20-25μm.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Additional Information: | RSMt 671.373 Aba p |
| Uncontrolled Keywords: | core projectile; W-Cu composit; powder metallurgy, core proyekti ; komposit W-C; metalurgi serbuk |
| Subjects: | Q Science > QC Physics > QC111 Density and specific gravity |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | - Davi Wah |
| Date Deposited: | 19 Mar 2019 01:55 |
| Last Modified: | 19 Mar 2019 01:55 |
| URI: | http://repository.its.ac.id/id/eprint/62527 |