Fajrin, Lum’atu Fi Rowwati (2016) Pengaruh Karbon Bambu Petung Terhadap Penyerapan Gelombang Mikro (8-12 Ghz) Bahan Magnetit (Fe3o4). Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
1112100703-presentationpdf.pdf - Published Version Download (2MB) | Preview |
Preview |
Text
1112100703-paperpdf.pdf - Published Version Download (326kB) | Preview |
Preview |
Text
1112100703-undergraduate-theses.pdf - Published Version Download (1MB) | Preview |
Abstract
Penelitian mengenai pengaruh karbon bambu petung
terhadap penyerapan gelombang mikro (8-12 GHz) yang
berbahan dasar magnetit (Fe3O4) telah dilakukan. Penelitian ini
dilakukan dengan tujuan mengetahui pengaruh karbon bambu
petung, besar penyerapan Fe3O4/C serta pebandingan
konsentrasi Fe3O4/C yang efisien. Proses sintesis dilakukan
dengan empat tahapan, yakni tahap separasi magnetik,
penggilingan bahan magnetik, karbonisasi dan pencampuran
mekanik. Karakterisasi yang digunakan antara lain XRF, XRD,
FTIR, SEM, VSM, LCR dan VNA. Dari hasil XRF menunjukkan
besar Fe setelah separasi magnetik sebesar 78,01%. Hasil XRD
bahan magnetik setelah proses penggilingan menunjukkan fasa
magnetit dengan rumus Fe3O4. Sedangkan untuk bambu
didapatkan fasa rGO (reduce oxide), dan hasil XRD kedua
campuran tersebut menunjukkan gabungan dari kedua fasa
tersebut. Karkaterisasi FTIR menunjukkan adanya ikatan C=C
yang merupakan ikatan dari fasa rGO. SEM menunjukkan bentuk
morfologi campuran Fe3O4 yang berbentuk kubik yang
bercampur dengan karbon yang berbentuk tak teratur dengan
permukaan yang berbentuk poros.LCR menunjukkan bahwa
campuran Fe3O4 dengan arang bambu petung merupakan bahan
semikonduktor. Sedangkan hasil VSM menunjukkan campuran
tersebut merupakan bahan hard magnetic. Dan karakterisasi
VNA yang menunjukkan bahwa penyerapan terbaesar terjadi
pada perbandingan Fe3O4:C sebesar 25%:75% dengan nilai
penyerapan sebesar -22.88 dB pada rentang frekuensi 8 – 9.14
GHz. Sehingga semakin banyak konsentrasi karbon yang
diberikan maka semakin besar nilai penyerapan yang dihasilkan.
===========================================================================================================
Research about the influence of carbon petung bamboo
on the microwave absorption of the magnetite (Fe3O4) material
has been performed. The objectives of the research are to
determine the effect of the carbon petung bamboo, the absorption
value of the Fe3O4/C, and ratio contain of Fe3O4/C most effective.
Synthesis process was carried out by four stages. Magnetic
separation, milling magnetic materials, carbonization, and
mechanical mixing.Structural characterization by XRF, XRD,
FTIR, LCR, VSM and VNA.XRF characterization was carried out
to determine the amount of Fe after magnetic separation. Amount
of the Fe after magnetic separation is 78,01%. The XRD’s result
of the milling magnetic materials showing the magnetite (Fe3O4)
meanwhile for the bamboo, XRD’s result showing the rGO phase,
and the XRD’s result for the mixture of them showing the
combination of their phase. FTIR characterization showing the
C=C bond which is the bond of rGO phase. From LCR were knew
the mixture of Fe3O4 with carbon petung bamboo is
semiconductor material. And VSM characterization showing the
mixture Fe3O4/C are hard magnetic material. SEM’s result
showing the morphological shape of the Fe3O4 which is cubicshaped
mixed with irregular-shaped of porous-surfaced carbon.
VNA characterization showed that the biggest absorption occur
at 25%:75% composition of the Fe3O4:C with absorption value -
22.88 dB within frequency range 9-9.14 GHz. We can concludethat the increasement of carbon concentration is followed by
increasement of the absorption value.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Additional Information: | RSFi 620.5 Faj p |
| Uncontrolled Keywords: | Karbon; Bambu Petung ; Gelombang Mikro ; Magnetit (Fe3o4) |
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) T Technology > TA Engineering (General). Civil engineering (General) > TA418.38 Materials--Fatigue. |
| Divisions: | Faculty of Mathematics and Science > Physics > 45201-(S1) Undergraduate Thesis |
| Depositing User: | EKO BUDI RAHARJO |
| Date Deposited: | 04 Oct 2019 02:28 |
| Last Modified: | 04 Oct 2019 02:28 |
| URI: | http://repository.its.ac.id/id/eprint/70983 |
Actions (login required)
 |
View Item |