Agusriyanto, Fajar Naufal (2020) Pengaruh Konsentrasi Inhibitor Obat Jenis Amlodipine Besylate dan pH Terhadap Perlindungan Korosi Baja Karbon Rendah di Media HCl. Other thesis, Institut Sepuluh Nopember.
Preview |
Text
02511640000149-Undergraduate_Thesis.pdf Download (3MB) | Preview |
Abstract
Korosi merupakan peristiwa terdegradasinya logam. Korosi sangatlah merugikan, maka dari itu dilakukan pengendalian dengan salah satu caranya ialah menggunakan inhibitor korosi merupakan zat yang apabila ditambahkan kedalam lingkungan korosif dapat menurunkan laju korosi yang terjadi pada logam. Amlodipine besylate memiliki kandungan yang dapat menghambat proses korosi. Oleh karena itu, pada penelitian ini digunakan amlodipine besylate sebagai inhibitor korosi pada baja karbon rendah yang direndam dalam media HCl. Penggunaan baja karbon rendah dikarenakan memiliki keuletan dan machinability yang baik. HCl biasa digunakan dalam proses pickling baja karbon rendah. Metode yang digunakan pada penelitian ini adalah polarisasi dan EIS. Hasil uji pada pH 1 didapatkan laju korosi terendah sebesar 0.129 mmpy dengan efisiensi 91% pada hari ke-5 dan pada pH 5 didapatkan laju korosi terendah sebesar 0.032 mmpy dengan efisiensi 87% pada hari ke-4. Mekanisme kerja inhibitor obat amlodipine besyalte secara mixed-type inhbitor yang lebih dominan sebagai inhibitor katodik dan adsorpsi yang terjadi secara adsorpsi fisik.
===================================================================================================================================
Corrosion is a metal degradated phenomenon. Corrosion is harmful, therefore preventation must be done by one of so many way using corrosion inhibitors. Corrosion inhibitors are subtance that if added into the corrosive environment could decrease the corrosion rate happened on metal. Amlodipine besylate has compounds can inhibit the corrosion process. Hence, this experiment used amlodipine besylate as corrosion inhibitor of low carbon steel in HCl media. Low carbon steel has good ductility and machinability. HCl is commonly used in low carbon steel pickling process. The methods used in this experiment are polarization and EIS. The result at pH 1 obtained the lowest corrosion rate of 0.129 mmpy with an efficiency of 91% on the 5th day and the result at pH 5 obtained the lowest corrosion rate of 0.032 mmpy with an efficiency of 87% on the 4th day. The mechanism of amlodipine besylate drug is mixed-type inhibitor but predominantly as a cathodic inhibitor and adsorption that occurs as physisorption.
| Item Type: | Thesis (Other) |
|---|---|
| Additional Information: | RSMt 620.112 23 Agu p-1 2020 |
| Uncontrolled Keywords: | Inhibitor korosi, Amlodipine besylate, Baja karbon rendah, HCl, Polarisasi, EIS |
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) > TA418.74 Corrosion and anti-corrosives |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | Fajar Naufal Agusriyanto |
| Date Deposited: | 07 Mar 2025 03:31 |
| Last Modified: | 07 Mar 2025 03:31 |
| URI: | http://repository.its.ac.id/id/eprint/73330 |
Actions (login required)
 |
View Item |