Riyadi, Muhammad Akbar Refoputra (2020) Analisis Perbandingan Hasil Pengelasan FCAW, GTAW, dan SMAW Pada Baja A36 Terhadap Uji Tarik, Uji Kekerasan, dan Struktur Mikro. Other thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
04311640000117-Undergraduate_Thesis.pdf Download (10MB) | Preview |
Preview |
Text
04311640000117-approval sheet.pdf Download (73kB) | Preview |
Abstract
Proses fabrikasi bangunan lepas pantai tidak pernah terlepas dari ada nya proses pengelasan. Pada konstruksi bangunan lepas pantai diperlukan suatu metode pengelasan yang tepat pada baja A36, dimana baja A36 adalah salah satu bahan utama pada proses fabrikasi bangunan lepas pantai. Pada penilitian ini dilakukan perbandingan hasil pengelasan FCAW, GTAW, dan SMAW pada baja A36 terhadap uji Tarik, uji kekerasan dan struktur mikro serta akan dilakukan pemilihan metode yang tepat berdasarkan analisis hasil uji mekanik dan biaya. Hasil dari penelitian ini adalah hasil uji tarik terbaik adalah metode pengelasan GTAW dengan ultimate strength rata-rata adalah 452,90 MPa, hasil uji kekerasan terbaik adalah metode pengelasan GTAW dengan hasil uji kekerasan pada weld metal adalah sebesar 177,02 HVN, pada pengujian mikro hasil struktur ferrite paling sedikit adalah pada metode pengelasan GTAW dengan hasil 67% dan struktur pearlite paling banyak adalah pada metode pengelasan GTAW dengan hasil 33%, serta metode pengelasan yang tepat pada baja A36 adalah metode pengelasan SMAW dikarenakan selisih hasil uji mekanik yang tidak besar dengan FCAW dan GTAW tetapi selisih biaya yang dikeluarkan memiliki selisih yang cukup besar ================================================================================================================================
Welding process is an important stages on offshore structure fabrication. In the construction of offshore structures required the existence of an appropriate welding method on A36 steel, because A36 steel is one of the main materials in the fabrication process of offshore structures. In this study there is a comparison of FCAW, GTAW, and SMAW on A36 steel against the tensile test, hardness test, and microstructure. The results of this study is the best tensile test results is the GTAW welding method with an average ultimate strength results of 452,90 MPa, the best hardness test results is the GTAW welding method with an average hardness test results of 477,02 HVN on weld metal, the most pearlite structure is the GTAW welding method with the results is 67%, and the fewest ferrite structure is the GTAW welding method with the results is 33%. The most proper welding method for A36 steel is the SMAW welding method because of small difference on mechanics result, but the price difference with FCAW and GTAW method is quite large.
| Item Type: | Thesis (Other) |
|---|---|
| Additional Information: | RSKe 671.52 Riy a-1 |
| Uncontrolled Keywords: | Pengelasan, Baja A36, FCAW, GTAW, SMAW, Uji Tarik, Uji Kekerasan, Uji Mikro |
| Subjects: | T Technology > TS Manufactures > TS227 Welding. |
| Divisions: | Faculty of Marine Technology (MARTECH) > Ocean Engineering > 38201-(S1) Undergraduate Thesis |
| Depositing User: | Muhammad Akbar Refoputra Riyadi |
| Date Deposited: | 20 Jun 2024 08:58 |
| Last Modified: | 21 Jun 2024 08:58 |
| URI: | http://repository.its.ac.id/id/eprint/74756 |
Actions (login required)
 |
View Item |