Desmelinda, Ersa (2015) Sitesis Dan Karakterisasi Listrik Material Ferroelektrik Bebas Timbal 0,8 (Ka0,5 Nao5 Nbo3)- 0,2 (Bao,3 Sr0,2 Ti O3) Dengan Metode Gabungan Reaksi Padat- Kopresipitasi Oksalat. Masters thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
1113201002-Master_Thesis.pdf - Accepted Version Download (3MB) | Preview |
Abstract
Material ferroelektrik bebas timbal dengan struktur ABO3 perovskite (A = K0,4 , Na0,4 ,
Ba0,16 , Sr0,04 and B = Nb0,8 , Ti0,2 ) telah berhasil disintesis dengan menggunakan metode
gabungan reaksi padat dan kopresipitasi oksalat. K0,5Na0,5NbO3 (KNN) yang disintesis dengan
metode reaksi padat dan Ba0,8Sr0,2 TiO3 (BST) berupa prekursor dan bubuk kalsinasi yang
disintesis dengan metode kopresipitasi oksalat dicampur dengan perbandingan mol 0,8KNN
dan 0,2BST dengan dua rute sintesis yaitu: KNN (kalsinasi) – BST (kalsinasi) sebagai rute
pertama dan KNN (kalsinasi) – BST (tanpa kalsinasi) sebagai rute kedua. Bubuk
(K0,4Na0,4 Ba0,16Sr0,04)(Nb0,8 Ti0,2 )O3 dari setiap rute dikalsinasi berdasarkan hasil analisis
termal (DTA-TGA). Fasa tunggal dari (K0,4 Na0,4Ba0,16 Sr0,04)(Nb0,8 Ti0,2 )O3 terbentuk dengan
kalsinasi 1100°C selama 2 jam untuk rute pertama dan 700°C selama 2 jam untuk rute kedua.
Perlakuan sintering dilakukan berdasarkan hasil dilatometri. Pelet yang telah disinter
menunjukkan pemadatan yang bagus dengan sintering pada suhu 1200°C selama 2 jam. Terkait
dengan volatilitas dari unsur alkali, dilakukan penambahan 4% mol K - 16% mol Na untuk rute
pertama dan 2% mol K - 8% mol Na untuk rute kedua sehingga fasa tunggal
(K0,4Na0,4 Ba0,16Sr0,04)(Nb0,8 Ti0,2 )O3 dalam bentuk pelet berhasil terbentuk. Setelah dilakukan
analisis struktur dengan metode Rietveld refinement, diketahui bahwa bubuk KNN berstruktur
perovskite orthorombik dengan a=3,572027 Å, b=3,570713 Å, c=3,565755 Å dan bubuk BST
berstruktur perovskite tetragonal dengan a=b=3,983412 Å, c=3,995775 Å. Diketahui pula
bahwa sampel (K0,4 Na0,4Ba0,16 Sr0,04)(Nb0,8Ti0,2 )O3 dalam bentuk pelet dari kedua rute sintesis
berstruktur perovskite tetragonal dengan parameter kisi a=b=3,956166 Å, c=3,981212 Å dari
rute pertama dan a=b=3,949728 Å, c=3,965926 Å dari rute kedua. Karakterisasi listrik dari
kedua sampel diidentifikasi dengan impedance analyser. (K0,4 Na0,4Ba0,16 Sr0,04)(Nb0,8Ti0,2 )O3
dari rute pertama memiliki suhu Curie ~440°C sedangkan dari rute kedua memiliki suhu Curie
~420°C. Terdapat dua daerah energi aktivasi berbeda untuk kedua sampel yaitu: 0,9297 eV
(~200°C - ~400°C) dan 1,4271 eV (~450°C - ~850°C) untuk sampel dari rute pertama dan
0,6419 eV (~200°C - ~400°C) dan 1,0397 eV (~450°C - ~850°C) untuk sampel dari rute kedua.
====================================================================================================
Lead free ferroelectric material behave ABO3 perovskite structure (A = K0.4 , Na0.4 ,
Ba0.16 , Sr0.04 and B = Nb0.8 , Ti0.2 ) has been successfully synthesized using a combination of
solid state reaction and oxalate coprecipitation method. A batch of K0.5Na0.5 NbO3 (KNN)
synthesized through solid state reaction and a batch of Ba0.8 Sr0.2 TiO3 (BST) precurcor-calcined
prepared via oxalate coprecipitation were mixed by 0.8 mol KNN and 0.2 mol BST for sample
synthesis into two different routes: KNN(calcined)-BST(calcined) as first route and
KNN(calcined)-BST (non calcined) as second route. (K0.4Na0.4 Ba0.16Sr0.04)(Nb0.8Ti0.2 )O3
powders from each route were calcined based on thermal analysis (DTA-TGA). Single phase of
(K0.4Na0.4 Ba0.16Sr0.04)(Nb0.8 Ti0.2 )O3 was formed by calcinations at 1100°C-2 hours for first
route and at 700°C-2 hours for second route. The study of sintering was conducted by mean
dilatometry. Sinter pellet sample shows good densification when sintering was took place at
1200°C for 2 hours. Due to volatility of alkaline element, K and Na were taken essesively by
increasing 4% mol K - 16% mol Na for first route and 2% mol K - 8% mol Na for second route.
Single phase of (K0.4Na0.4 Ba0.16 Sr0.04 )(Nb0.8 Ti0.2 )O3 pellet has been obtained successfully.
After structure analysis using Rietveld refinements, known that KNN powder behave
perovskite orthorombic structure with a=3.572027 Å, b=3.570713 Å, c=3.565755 Å and BST
powder behave perovskite tetragonal structure with a=b=3.983412 Å, c=3.995775 Å. It also
known that (K0.4Na0.4 Ba0.16 Sr0.04 )(Nb0.8 Ti0.2 )O3 pellets from both routes behave perovskite
tetragonal structure with lattice parameter a=b=3.956166 Å, c=3.981212 Å for first route and
a=b=3.949728 Å, c=3.965926 Å for second route. Electrical properties was identified by
impedance analyzer. Curie temperature of (K0.4Na0.4 Ba0.16 Sr0.04 )(Nb0.8 Ti0.2 )O3 from first route
is ~440°C and ~420°C for second route. There are two activation energy region of both sample:
-0.9297 eV (~200°C - ~400°C) and 1.4271 eV (~450°C - ~850°C) for sample by first route and
0.6419 eV (~200°C - ~400°C) and 1.0397 eV (~450°C - ~850°C) for sample by second route.
| Item Type: | Thesis (Masters) |
|---|---|
| Additional Information: | RTFi 537.24 Des s 3100016063903 |
| Uncontrolled Keywords: | dielectricity, coprecipitation, perovskite, oxalate, |
| Subjects: | Q Science > QC Physics > QC1 Dielectrics |
| Divisions: | Faculty of Mathematics and Science > Physics > 45101-(S2) Master Thesis |
| Depositing User: | - Davi Wah |
| Date Deposited: | 13 Feb 2020 03:29 |
| Last Modified: | 14 Feb 2020 02:47 |
| URI: | http://repository.its.ac.id/id/eprint/74867 |
Actions (login required)
 |
View Item |