Pengaruh Karbon Bambu Petung Terhadap Penyerapan Gelombang Mikro (8-12 Ghz) Bahan Magnetit (Fe3o4)

Fajrin, Lum’atu Fi Rowwati (2016) Pengaruh Karbon Bambu Petung Terhadap Penyerapan Gelombang Mikro (8-12 Ghz) Bahan Magnetit (Fe3o4). Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
1112100703-presentationpdf.pdf - Published Version

Download (2MB) | Preview
[img]
Preview
Text
1112100703-paperpdf.pdf - Published Version

Download (326kB) | Preview
[img]
Preview
Text
1112100703-undergraduate-theses.pdf - Published Version

Download (1MB) | Preview

Abstract

Penelitian mengenai pengaruh karbon bambu petung terhadap penyerapan gelombang mikro (8-12 GHz) yang berbahan dasar magnetit (Fe3O4) telah dilakukan. Penelitian ini dilakukan dengan tujuan mengetahui pengaruh karbon bambu petung, besar penyerapan Fe3O4/C serta pebandingan konsentrasi Fe3O4/C yang efisien. Proses sintesis dilakukan dengan empat tahapan, yakni tahap separasi magnetik, penggilingan bahan magnetik, karbonisasi dan pencampuran mekanik. Karakterisasi yang digunakan antara lain XRF, XRD, FTIR, SEM, VSM, LCR dan VNA. Dari hasil XRF menunjukkan besar Fe setelah separasi magnetik sebesar 78,01%. Hasil XRD bahan magnetik setelah proses penggilingan menunjukkan fasa magnetit dengan rumus Fe3O4. Sedangkan untuk bambu didapatkan fasa rGO (reduce oxide), dan hasil XRD kedua campuran tersebut menunjukkan gabungan dari kedua fasa tersebut. Karkaterisasi FTIR menunjukkan adanya ikatan C=C yang merupakan ikatan dari fasa rGO. SEM menunjukkan bentuk morfologi campuran Fe3O4 yang berbentuk kubik yang bercampur dengan karbon yang berbentuk tak teratur dengan permukaan yang berbentuk poros.LCR menunjukkan bahwa campuran Fe3O4 dengan arang bambu petung merupakan bahan semikonduktor. Sedangkan hasil VSM menunjukkan campuran tersebut merupakan bahan hard magnetic. Dan karakterisasi VNA yang menunjukkan bahwa penyerapan terbaesar terjadi pada perbandingan Fe3O4:C sebesar 25%:75% dengan nilai penyerapan sebesar -22.88 dB pada rentang frekuensi 8 – 9.14 GHz. Sehingga semakin banyak konsentrasi karbon yang diberikan maka semakin besar nilai penyerapan yang dihasilkan. =========================================================================================================== Research about the influence of carbon petung bamboo on the microwave absorption of the magnetite (Fe3O4) material has been performed. The objectives of the research are to determine the effect of the carbon petung bamboo, the absorption value of the Fe3O4/C, and ratio contain of Fe3O4/C most effective. Synthesis process was carried out by four stages. Magnetic separation, milling magnetic materials, carbonization, and mechanical mixing.Structural characterization by XRF, XRD, FTIR, LCR, VSM and VNA.XRF characterization was carried out to determine the amount of Fe after magnetic separation. Amount of the Fe after magnetic separation is 78,01%. The XRD’s result of the milling magnetic materials showing the magnetite (Fe3O4) meanwhile for the bamboo, XRD’s result showing the rGO phase, and the XRD’s result for the mixture of them showing the combination of their phase. FTIR characterization showing the C=C bond which is the bond of rGO phase. From LCR were knew the mixture of Fe3O4 with carbon petung bamboo is semiconductor material. And VSM characterization showing the mixture Fe3O4/C are hard magnetic material. SEM’s result showing the morphological shape of the Fe3O4 which is cubicshaped mixed with irregular-shaped of porous-surfaced carbon. VNA characterization showed that the biggest absorption occur at 25%:75% composition of the Fe3O4:C with absorption value - 22.88 dB within frequency range 9-9.14 GHz. We can concludethat the increasement of carbon concentration is followed by increasement of the absorption value.

Item Type: Thesis (Undergraduate)
Additional Information: RSFi 620.5 Faj p
Uncontrolled Keywords: Karbon; Bambu Petung ; Gelombang Mikro ; Magnetit (Fe3o4)
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
T Technology > TA Engineering (General). Civil engineering (General) > TA418.38 Materials--Fatigue.
Divisions: Faculty of Mathematics and Science > Physics > 45201-(S1) Undergraduate Thesis
Depositing User: EKO BUDI RAHARJO
Date Deposited: 04 Oct 2019 02:28
Last Modified: 04 Oct 2019 02:28
URI: https://repository.its.ac.id/id/eprint/70983

Actions (login required)

View Item View Item